Abstract

Scratch testing using nanoindentation helps to characterize material's wear resistance and the accompanying material removal, and deformation mechanism. The effect of load and repeated scratching on pure zinc was investigated in this study. Surface examination post scratching revealed formation of long chips at lower loads which can be attributed to ductile-like behavior. Ploughing dominated at higher loads while micro-cutting was active at lower loads. The material removal factor (fab) is an indicator of the prevailing wear mechanism. A good correlation appeared between the observed wear mechanism and the calculated fab, wherein interplay of ploughing and microcutting was observed. The decrease in wear rate as the number of passes increased and the decreasing value of fab, is indicative of the strain hardening behavior during repeated scratching. The presence of intergranular fracture, slip and twinning on the deformed surface is indicative of the material's response to induced stress.

This content is only available via PDF.

Article PDF first page preview

Article PDF first page preview
You do not currently have access to this content.