Self-lubricating composite NiAl–Cr–Mo–CaF2–Ag was fabricated by powder metallurgy technique. The NiAl matrix composite with 10 wt.% Ag provides self-lubricating properties at a broad temperature range between room temperature and 1000 °C. Especially at 800 °C, the composite offers excellent friction reduction about 0.2 and wear resistance about 0.7 × 10−4 mm3 N−1 m−1. The lubricous behavior at a wide temperature range could be attributed to the synergistic effect of Ag, CaF2, CaCrO4, and CaMoO4.
Issue Section:
Coatings & Solid Lubricants
References
1.
Dellacorte
, C.
, Sliney
, H. E.
, Bogdanski
, M. S.
, and Dellacorte
, C.
, 1992
, “Tribological and Mechanical Comparison of Sintered and HIPped PM212: High Temperature Self-Lubricating Composites
,” Technical Report No. NASA-TM-X-105379.2.
Dellacorte
, C.
, and Fellenstein
, J. A.
, 1997
, “The Effect of Compositional Tailoring on the Thermal Expansion and Tribological Properties of PS300: A Solid Lubricant Composite Coating
,” Tribol. Trans.
, 40
(4
), pp. 639
–642
.10.1080/104020097089837033.
Blanchet
, T. A.
, Kim
, J. H.
, Calabrese
, S. J.
, and DellaCorte
, C.
, 2002
, “Thrust-Washer Evaluation of Self-Lubricating PS304 Composite Coatings in High Temperature Sliding contact
,” Tribol. Trans.
, 45
(4), pp. 491
–498
.10.1080/104020002089825794.
Ding
, C. H.
, Li
, P. L.
, Ran
, G.
, Tian
, Y. W.
, and Zhou
, J. N.
, 2007
, “Tribological Property of Self-Lubricating PM304 Composite
,” Wear
, 262
(5–6
), pp. 575
–581
.10.1016/j.wear.2006.07.0035.
Ouyang
, J. H.
, Li
, Y. F.
, Wang
, Y. M.
, Zhou
, Y.
, Murakami
, T.
, and Sasakic
, S.
, 2009
, “Microstructure and Tribological Properties of ZrO2(Y2O3) Matrix Composites Doped With Different Solid Lubricants From Room Temperature to 800 °C
,” Wear
, 267
(9–10), pp. 1353
–1360
.10.1016/j.wear.2008.11.0176.
Jin
, Y.
, Kato
, K.
, and Umehara
, N.
, 1999
, “Effects of Sintering Aids and Solid Lubricants on Tribological Behaviours of CMC/Al2O3 Pair at 650 °C
,” Tribol. Lett.
, 6
(1), pp. 15
–21
.10.1023/A:10191951200427.
Skopp
, A.
, Woydt
, M.
, and Habig
, K.-H.
, 1995
, “Tribological Behavior of Silicon Nitride Materials Under Unlubricated Sliding Between 22 °C and 1000 °C
,” Wear
, 181–183
(2
), pp. 571
–580
.10.1016/0043-1648(95)90173-68.
Kong
, L. Q.
, Bi
, Q. L.
, Zhu
, S. Y.
, Yang
, J.
, and Liu
, W. M.
, 2012
, “Tribological Properties of ZrO2(Y2O3)–Mo–BaF2/CaF2 Composites at High Temperatures
,” Tribol. Int.
, 45
(1
), pp. 43
–49
.10.1016/j.triboint.2011.09.0089.
Kong
, L. Q.
, Bi
, Q. L.
, Niu
, M. Y.
, Zhu
, S. Y.
, Yang
, J.
, and Liu
, W. M.
, 2013
, “High-Temperature Tribological Behavior of ZrO2–MoS2–CaF2 Self-Lubricating Composites
,” J. Eur. Ceram. Soc.
, 33
(1
), pp. 51
–59
.10.1016/j.jeurceramsoc.2012.08.00310.
Ward-Close
, C. M.
, Minorb
, R.
, and Doorbarb
, P. J.
, 1996
, “Intermetallic-Matrix Composites—A Review
,” Intermetallics
, 4
(3), pp. 217
–229
.10.1016/0966-9795(95)00037-211.
Yamaguchi
, M.
, Inui
, H.
, and Ito
, K.
, 2000
, “High Temperature Structural Intermetallics
,” Acta Mater.
, 48
(1
), pp. 307
–322
.10.1016/S1359-6454(99)00301-812.
Deevi
, S. C.
, Sikkat
, V. K.
, and Liu
, C. T.
, 1991
, “Processing, Properties, and Applications of Nickel and Iron Aluminides
,” Prog. Mater. Sci.
, 42
(1–4), pp. 177
–192
.10.1016/S0079-6425(97)00014-513.
Zhu
, S. Y.
, Bi
, Q. L.
, Yang
, J.
, Liu
, W. M.
, and Xue
, Q. J.
, 2011
, “Ni3Al Matrix High Temperature Self-Lubricating Composites
,” Tribol. Int.
, 44
(4), pp. 445
–453
.10.1016/j.triboint.2010.11.01614.
Zhu
, S. Y.
, Bi
, Q. L.
, Yang
, J.
, Liu
, W. M.
, and Xue
, Q. J.
, 2011
, “Effect of Particle Size on Tribological Behavior of Ni3Al Matrix High Temperature Self-Lubricating Composites
,” Tribol. Int.
, 44
(12), pp. 1800
–1809
.10.1016/j.triboint.2011.07.00215.
Zhu
, S. Y.
, Bi
, Q. L.
, Kong
, L. Q.
, Yang
, J.
, and Liu
, W. M.
, 2012
, “Barium Chromate as a Solid Lubricant for Nickel Aluminum
,” Tribol. Trans.
, 55
(2), pp. 218
–223
.10.1080/10402004.2011.64385516.
Zhu
, S. Y.
, Bi
, Q. L.
, Wu
, H. R.
, Yang
, J.
, and Liu
, W. M.
, 2011
, “NiAl Matrix High Temperature Self-Lubricating Composite
,” Tribol. Lett.
, 41
(3), pp. 535
–540
.10.1007/s11249-010-9727-917.
Zhu
, S. Y.
, Bi
, Q. L.
, Niu
, M. Y.
, Yang
, J.
, and Liu
, W. M.
, 2012
, “Tribological Behavior of NiAl Matrix Composites With Addition of Oxides at High Temperatures
,” Wear
, 274–275
(1), pp. 423
–434
.10.1016/j.wear.2011.11.00618.
Deadmore
, D. L.
, and Sliney
, H. E.
, 1987
, “Hardness of CaF2 and BaF2 Solid Lubricants at 25–670 °C
,” Report No. NASA-TM-88979.19.
Sliney
, H. E.
, and Graham
, J. W.
, 1974
, “Tribological Properties of Self-Lubricating Fluoride-Metal Composites to 900 °C (1650°F)—A Review and Some New Developments
,” Report No. NASA-TM-X-71575.Copyright © 2015 by ASME
You do not currently have access to this content.