Self-lubricating composite NiAl–Cr–Mo–CaF2–Ag was fabricated by powder metallurgy technique. The NiAl matrix composite with 10 wt.% Ag provides self-lubricating properties at a broad temperature range between room temperature and 1000 °C. Especially at 800 °C, the composite offers excellent friction reduction about 0.2 and wear resistance about 0.7 × 10−4 mm3 N−1 m−1. The lubricous behavior at a wide temperature range could be attributed to the synergistic effect of Ag, CaF2, CaCrO4, and CaMoO4.

References

References
1.
Dellacorte
,
C.
,
Sliney
,
H. E.
,
Bogdanski
,
M. S.
, and
Dellacorte
,
C.
,
1992
, “
Tribological and Mechanical Comparison of Sintered and HIPped PM212: High Temperature Self-Lubricating Composites
,” Technical Report No. NASA-TM-X-105379.
2.
Dellacorte
,
C.
, and
Fellenstein
,
J. A.
,
1997
, “
The Effect of Compositional Tailoring on the Thermal Expansion and Tribological Properties of PS300: A Solid Lubricant Composite Coating
,”
Tribol. Trans.
,
40
(
4
), pp.
639
642
.10.1080/10402009708983703
3.
Blanchet
,
T. A.
,
Kim
,
J. H.
,
Calabrese
,
S. J.
, and
DellaCorte
,
C.
,
2002
, “
Thrust-Washer Evaluation of Self-Lubricating PS304 Composite Coatings in High Temperature Sliding contact
,”
Tribol. Trans.
,
45
(4), pp.
491
498
.10.1080/10402000208982579
4.
Ding
,
C. H.
,
Li
,
P. L.
,
Ran
,
G.
,
Tian
,
Y. W.
, and
Zhou
,
J. N.
,
2007
, “
Tribological Property of Self-Lubricating PM304 Composite
,”
Wear
,
262
(
5–6
), pp.
575
581
.10.1016/j.wear.2006.07.003
5.
Ouyang
,
J. H.
,
Li
,
Y. F.
,
Wang
,
Y. M.
,
Zhou
,
Y.
,
Murakami
,
T.
, and
Sasakic
,
S.
,
2009
, “
Microstructure and Tribological Properties of ZrO2(Y2O3) Matrix Composites Doped With Different Solid Lubricants From Room Temperature to 800 °C
,”
Wear
,
267
(9–10), pp.
1353
1360
.10.1016/j.wear.2008.11.017
6.
Jin
,
Y.
,
Kato
,
K.
, and
Umehara
,
N.
,
1999
, “
Effects of Sintering Aids and Solid Lubricants on Tribological Behaviours of CMC/Al2O3 Pair at 650 °C
,”
Tribol. Lett.
,
6
(1), pp.
15
21
.10.1023/A:1019195120042
7.
Skopp
,
A.
,
Woydt
,
M.
, and
Habig
,
K.-H.
,
1995
, “
Tribological Behavior of Silicon Nitride Materials Under Unlubricated Sliding Between 22 °C and 1000 °C
,”
Wear
,
181–183
(
2
), pp.
571
580
.10.1016/0043-1648(95)90173-6
8.
Kong
,
L. Q.
,
Bi
,
Q. L.
,
Zhu
,
S. Y.
,
Yang
,
J.
, and
Liu
,
W. M.
,
2012
, “
Tribological Properties of ZrO2(Y2O3)–Mo–BaF2/CaF2 Composites at High Temperatures
,”
Tribol. Int.
,
45
(
1
), pp.
43
49
.10.1016/j.triboint.2011.09.008
9.
Kong
,
L. Q.
,
Bi
,
Q. L.
,
Niu
,
M. Y.
,
Zhu
,
S. Y.
,
Yang
,
J.
, and
Liu
,
W. M.
,
2013
, “
High-Temperature Tribological Behavior of ZrO2–MoS2–CaF2 Self-Lubricating Composites
,”
J. Eur. Ceram. Soc.
,
33
(
1
), pp.
51
59
.10.1016/j.jeurceramsoc.2012.08.003
10.
Ward-Close
,
C. M.
,
Minorb
,
R.
, and
Doorbarb
,
P. J.
,
1996
, “
Intermetallic-Matrix Composites—A Review
,”
Intermetallics
,
4
(3), pp.
217
229
.10.1016/0966-9795(95)00037-2
11.
Yamaguchi
,
M.
,
Inui
,
H.
, and
Ito
,
K.
,
2000
, “
High Temperature Structural Intermetallics
,”
Acta Mater.
,
48
(
1
), pp.
307
322
.10.1016/S1359-6454(99)00301-8
12.
Deevi
,
S. C.
,
Sikkat
, V
. K.
, and
Liu
,
C. T.
,
1991
, “
Processing, Properties, and Applications of Nickel and Iron Aluminides
,”
Prog. Mater. Sci.
,
42
(1–4), pp.
177
192
.10.1016/S0079-6425(97)00014-5
13.
Zhu
,
S. Y.
,
Bi
,
Q. L.
,
Yang
,
J.
,
Liu
,
W. M.
, and
Xue
,
Q. J.
,
2011
, “
Ni3Al Matrix High Temperature Self-Lubricating Composites
,”
Tribol. Int.
,
44
(4), pp.
445
453
.10.1016/j.triboint.2010.11.016
14.
Zhu
,
S. Y.
,
Bi
,
Q. L.
,
Yang
,
J.
,
Liu
,
W. M.
, and
Xue
,
Q. J.
,
2011
, “
Effect of Particle Size on Tribological Behavior of Ni3Al Matrix High Temperature Self-Lubricating Composites
,”
Tribol. Int.
,
44
(12), pp.
1800
1809
.10.1016/j.triboint.2011.07.002
15.
Zhu
,
S. Y.
,
Bi
,
Q. L.
,
Kong
,
L. Q.
,
Yang
,
J.
, and
Liu
,
W. M.
,
2012
, “
Barium Chromate as a Solid Lubricant for Nickel Aluminum
,”
Tribol. Trans.
,
55
(2), pp.
218
223
.10.1080/10402004.2011.643855
16.
Zhu
,
S. Y.
,
Bi
,
Q. L.
,
Wu
,
H. R.
,
Yang
,
J.
, and
Liu
,
W. M.
,
2011
, “
NiAl Matrix High Temperature Self-Lubricating Composite
,”
Tribol. Lett.
,
41
(3), pp.
535
540
.10.1007/s11249-010-9727-9
17.
Zhu
,
S. Y.
,
Bi
,
Q. L.
,
Niu
,
M. Y.
,
Yang
,
J.
, and
Liu
,
W. M.
,
2012
, “
Tribological Behavior of NiAl Matrix Composites With Addition of Oxides at High Temperatures
,”
Wear
,
274–275
(1), pp.
423
434
.10.1016/j.wear.2011.11.006
18.
Deadmore
,
D. L.
, and
Sliney
,
H. E.
,
1987
, “
Hardness of CaF2 and BaF2 Solid Lubricants at 25–670 °C
,” Report No. NASA-TM-88979.
19.
Sliney
,
H. E.
, and
Graham
,
J. W.
,
1974
, “
Tribological Properties of Self-Lubricating Fluoride-Metal Composites to 900 °C (1650°F)—A Review and Some New Developments
,” Report No. NASA-TM-X-71575.
You do not currently have access to this content.