The influence of alumina and titanium carbide, components of magnetic recording sliders, on the carbon gasification reaction was investigated. Pure alumina and titanium carbide powders were each combined with graphite powder and subjected to thermogravimetric analysis (TGA). The molar ratio ranged from 0 to 20 mol percent; graphite powder was the balance. From the thermogravimetric analysis, the activation energy of the reactions was determined. It was found that the activation energy for carbon gasification reduced slightly for increasing alumina mole percentage. Titanium carbide additions markedly increased the activation energy. This increase indicates a competitive oxidation reaction that forms titanium oxide, as confirmed by X-ray diffraction (XRD). As a result of these observations, titanium oxide was also mixed with graphite powders and analyzed by TGA. Titanium oxide has an activation energy behavior that becomes more complex with increasing mole percentage: the activation energy first increases and then decreases. These data are presented and the oxidation reaction is proposed.
The Effects of Slider Material on the Gasification of Carbon
Contributed by the Tribology Division for publication in the ASME JOURNAL OF TRIBOLOGY. Manuscript received by the Tribology Division October 27, 1998; revised manuscript received November 13, 2001. Associate Editor: A. K. Menon.
- Views Icon Views
- Share Icon Share
- Cite Icon Cite
- Search Site
Ramirez, A. G., Sinclair, R., Harkins , C. G., and Lin, A. R. (September 24, 2002). "The Effects of Slider Material on the Gasification of Carbon ." ASME. J. Tribol. October 2002; 124(4): 771–774. https://doi.org/10.1115/1.1467613
Download citation file:
- Ris (Zotero)
- Reference Manager