Fracture toughness tests were conducted for carbon composite scarf joints with and without carbon nanotube (CNT) reinforcement in order to study the effect of CNT on enhancing the fracture toughness of the scarf joint interface. Both mode I (i.e., opening mode) and mode II (i.e., shear mode) fracture tests were undertaken with and without CNT applied locally at the joint interface. During the study, the image correlation technique was used to examine the fracture mechanisms altered by the introduction of CNT. The experimental study showed that CNT increased the fracture toughness of the composite interface significantly, especially for the mode II fracture, with altering the fracture mechanism. On the other hand, there was no significant change on mode I fracture caused by CNT reinforcement. The enhancement of mode II fracture toughness was considered to result from the mechanical interlocking between polymers and CNT at the scarf joint interface.
Skip Nav Destination
Article navigation
April 2011
Research Papers
Fracture Toughness of Composite Joints With Carbon Nanotube Reinforcement
S. D. Faulkner,
S. D. Faulkner
Department of Mechanical & Aerospace Engineering,
Naval Postgraduate School
, Monterey, CA 93943
Search for other works by this author on:
Y. W. Kwon
Y. W. Kwon
Department of Mechanical & Aerospace Engineering,
Naval Postgraduate School
, Monterey, CA 93943
Search for other works by this author on:
S. D. Faulkner
Department of Mechanical & Aerospace Engineering,
Naval Postgraduate School
, Monterey, CA 93943
Y. W. Kwon
Department of Mechanical & Aerospace Engineering,
Naval Postgraduate School
, Monterey, CA 93943J. Pressure Vessel Technol. Apr 2011, 133(2): 021002 (5 pages)
Published Online: February 9, 2011
Article history
Received:
August 6, 2008
Revised:
December 18, 2008
Online:
February 9, 2011
Published:
February 9, 2011
Citation
Faulkner, S. D., and Kwon, Y. W. (February 9, 2011). "Fracture Toughness of Composite Joints With Carbon Nanotube Reinforcement." ASME. J. Pressure Vessel Technol. April 2011; 133(2): 021002. https://doi.org/10.1115/1.4002676
Download citation file:
Get Email Alerts
Cited By
Surface Strain Measurement for Non-Intrusive Internal Pressure Evaluation of A Cannon
J. Pressure Vessel Technol
The Upper Bound of the Buckling Stress of Axially Compressed Carbon Steel Circular Cylindrical Shells
J. Pressure Vessel Technol (December 2024)
Crack Growth Prediction Based on Uncertain Parameters Using Ensemble Kalman Filter
J. Pressure Vessel Technol (December 2024)
Defect Detection of Polyethylene Gas Pipeline Based on Convolutional Neural Networks and Image Processing
J. Pressure Vessel Technol
Related Articles
Fracture Toughness of Highly Ordered Carbon Nanotube/Alumina Nanocomposites
J. Eng. Mater. Technol (July,2004)
Analysis of Crack Propagation in Fixed-Free Single-Walled Carbon Nanotube Under Tensile Loading Using XFEM
J. Nanotechnol. Eng. Med (November,2010)
Tailoring the Microstructure of a Metal-Reinforced Ceramic Matrix Composite
J. Eng. Mater. Technol (July,2000)
Evaluation of the Fracture Toughness of Short Carbon Fiber Reinforced Thermoplastic Composites
J. Eng. Mater. Technol (April,2024)
Related Proceedings Papers
Related Chapters
Applications of Elastic-Plastic Fracture Mechanics in Section XI, ASME Code Evaluations
Online Companion Guide to the ASME Boiler & Pressure Vessel Codes
Characterization of Ultra-High Temperature and Polymorphic Ceramics
Advanced Multifunctional Lightweight Aerostructures: Design, Development, and Implementation
Impact Testing
A Quick Guide to API 510 Certified Pressure Vessel Inspector Syllabus