Investigation of environmental cracking of a 1100-MPa yield strength A723 steel cannon tube subjected to prototype firings is described. Metallographic results show cracking of the steel beneath a 0.12-mm protective layer of chromium. Cracks undermine and remove sections of chromium and lead to localized erosion that ruins the cannon. Key features of the firing thermal damage and cracking are: (i) recrystalization of the chromium to a depth of up to 0.08 mm; (ii) steel transformation to 0.19 mm below the chrome surface; (iii) two different periodic arrays of cracks normal to the hoop and axial directions, with mean depths of 0.23 and 0.46 mm, respectively. Time-temperature-depth profiles for the firing cycle were derived via bi-material finite difference analysis of a semi-infinite solid which incorporated cannon combustion gas temperatures and material properties that vary as a function of temperature. The temperature and depth associated with the steel transformation were used to solve iteratively for the convective heat transfer coefficient. This value was further confirmed by the depths of chromium recrystalization and of the crack arrays in the two orientations. A profile of maximum temperature versus depth is used to determine the near-bore applied and residual stress distributions within the tube. The measured volume change of steel transformation is used to determine an upper limit on applied and residual stresses. These stresses are used to determine crack-tip stress intensity factors for the observed crack arrays, and hence provide some explanation for the differential depths of cracking. The near-bore temperature and residual stress distributions are used to help determine the cause of hydrogen cracking and measures to prevent cracking. Compressive yielding due to thermal loading produces near-bore tensile residual stresses, and thereby causes hydrogen cracking. Prevention of cracking is discussed in relationship to hydrogen crack growth rate tests of alternative alloys and coatings.

Issue Section:
Research Papers
Topics:
Artillery, Hydrogen embrittlement, Cracking (Materials), Fracture (Materials), Fracture (Process), Temperature, Steel, Stress, Firing, Residual stresses, Alloys, Coatings, Combustion gases, Convection, Cycles, Damage, Engineering prototypes, Erosion, Hydrogen, Materials properties, Yield strength
1.
Andrasic, C. P., and Parker, A. P., 1982, “Spline Fit Weight Function Data for Cracked Thick Cylinders,” Royal Military College of Science Technical Note MAT/36, Shrivenham, England.
2.
Andrasic
C. P.
, and
Parker
A. P.
,
1984
, “
Dimensionless Stress Intensity Factors for Cracked Thick Cylinders Under Polynomial Crack Face Loadings
,”
Engineering Fracture Mechanics
, Vol.
19
,
1
, pp.
187
–
193
.
3.
Dunn, S., Sopok, S., Coats, D., O’Hara, P., Nickerson, G., and Pflegl, G., 1995, “Unified Computer Model for Predicting Thermochemical Erosion in Gun Barrels,” US Army ARDEC, Bene´t Laboratories, ARCCB-TR-95030.
4.
Fisher, E. B., 1996, “Gun Barrel Heating and Wear Environment,” Proceedings, 42nd Sagamore Workshop on Gun Barrel Wear and Erosion, July 29–31, pp. 591–611. US Army, Aberdeen Proving Ground, MD.
5.
Gough, J. P., and Morrison, J., 1984, “Craze Cracking in 105 mm Artillery and Tank Gun Barrels,” Canadian Defence Research Establishment Pacific, Technical Memorandum 84–9.
6.
Hehmann, R. F., 1968, “The Bainite Transformation,” Phase Transformations, American Society for Metals, Metals Park, OH, Chap. 9.
7.
Incropea, F. P., and DeWitt, D. P., 1985, Introduction to Heat Transfer, Wiley, New York, NY, pp. 259–263.
8.
Marcinkowski, M. J., 1959, “Plastic Deformation of Chromium at Low Temperatures,” Aeronautical Research Laboratory, Wright-Patterson AFB, WADC TR 50-294; (AD2116260).
9.
Parker, A. P., 1998, “Stability of Arrays of Multiple Edge Cracks,” Army Armament RD&E Center, Watervliet Technical Report, to be published in Engineering Fracture Mechanics.
10.
Parker, A. P., and Underwood, J. H., 1998, “Influence of Bauschinger Effect on Residual Stress and Fatigue Lifetimes in Autofrettaged Thick Walled Cylinders,” Fatigue and Fracture Mechanics: 29th Volume, ASTM STP 1321, T. L. Panontin and S. D. Sheppard, eds., American Society for Testing and Materials, Metals Park, OH.
11.
Reed-Hill, R. E., 1964, Physical Metallurgy Principles, Van Nostrand, pp. 503–504.
12.
Sopok, S., O’Hara, P., Vottis, P., Pflegl, G., Rickard, C., and Loomis, R., 1997, “Erosion Modeling of the 120-MM M256.M829A2 Gun System,” Army Armament RD&E Center, Watervliet, ARCCB-TR-97011, 1997, presented at ADPA Gun and Ammunition Symposium, San Diego, CA, April 7-10.
13.
Thornton, P. A., and Colangelo, V. J., 1985, Fundamentals of Engineering Materials, Prentice Hall, Englewood Cliffs, NJ, p. 419, Figs. 12–18 (courtesy P. J. Cote).
14.
Underwood
J. H.
, and
Parker
A. P.
,
1995
, “
Fatigue Life Analyses and Tests for Thick-Wall Cylinders Including Effects of Overstrain and Axial Grooves
,”
ASME JOURNAL OF PRESSURE VESSEL TECHNOLOGY
, Vol.
117
, pp.
222
–
226
.
15.
Vigilante, G. N., Underwood, J. H., Crayon, D., Tauscher, S., Sage, T., and Troiano, E., 1997, “Hydrogen Induced Cracking Tests of High Strength Steels and Nickel-Iron Base Alloys using the Bolt-Loaded Specimen,” Fatigue and Fracture Mechanics: 28th Volume, ASTM STP 1321, American Society for Testing and Materials, pp. 602–616.
This content is only available via PDF.
Copyright © 1999
 by The American Society of Mechanical Engineers
You do not currently have access to this content.