The effect of water flow rate upon the environmentally assisted cracking (EAC) response of a high-sulfur ferritic steel was studied at a temperature of 243°C. In contrast to earlier studies which employed compact-type specimens, this study employed relatively large tight semi-elliptical surface cracks tested under generally linear-elastic conditions. Flow velocities parallel to the crack as low as 1.58–1.84 m/s were effective in mitigating EAC.

1.
Atkinson, J. D., and Forrest, J. E., 1986, “The Role of MnS Inclusions in the Development of Environmentally Assisted Cracking of Nuclear Reactor Pressure Vessel Steels,” Proceedings, Second International Atomic Energy Agency Specialists’ Meeting on Subcritical Crack Growth, NUREG/CP-0067, Vol. 2, pp. 153–178.
2.
Bamford, W. H., and Wilson, I. L. W., 1986, “Characterization of the Environmental Cracking Behavior of High Sulfur Plates,” ibid., Vol. 1, pp. 317–338.
3.
Bulloch
J. H.
,
1986
, “
Environmental Fatigue Crack Growth Studies: The Effects of Non-Metallic Inclusions
,”
Res Mechanica
, Vol.
18
, pp.
331
354
.
4.
Bulloch
J. H.
,
1988
, “
The Influence of Manganese Sulphide Inclusions on Environmental Assisted Crack Growth Behaviour: Fractographic Aspects
,”
Theoretical and Applied Fracture Mechanics
, Vol.
10
, No.
2
, pp.
89
95
.
5.
Choi
H.
,
Beck
F. H.
,
Szklarska-Smialowska
Z.
, and
Macdonald
D. D.
,
1982
, “
The Effect of Fluid Flow on the Stress Corrosion Cracking of ASTM A508 Cl 2 Steel and AISI Type 304 Stainless Steel in High Temperature Water
,”
Corrosion
, Vol.
38
, No.
2
, pp.
76
85
.
6.
Combrade, P., Foucault, M., and Slama, G., 1988, “Effect of Sulfur on the Fatigue Crack Growth Rates of Pressure Vessel Steel Exposed to PWR Coolant: Preliminary Model for Prediction of the Transitions Between High and Low Crack Growth Rates,” Proceedings, Third International Symposium on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, Met. Soc. of AIME, pp. 269–276.
7.
Cullen, W. H., Kemppainen, M., Ha¨nninen, and To¨rro¨nen, K., 1985, “The Effects of Sulfur Chemistry and Flow Rate on Fatigue Crack Growth Rates in LWR Environments,” NUREG/CR-4121.
8.
Eason
E. A.
,
Andrew
S. P.
,
Warmbrodt
S. B.
,
Nelson
E. E.
, and
Gilman
J. D.
,
1989
, “
Analysis of Pressure Vessel Steel Fatigue Tests in Air
,”
Nuclear Engineering and Design
, Vol.
115
, No.
1
, pp.
23
30
.
9.
Eason, E. A., Nelson, E. E., and Gilman, J. D., 1990, “Reactor Pressure Vessel Steel Fatigue Crack Growth Rates in Air and Water Environments,” Proceedings, Third International Atomic Energy Agency Specialists’ Meeting on Subcritical Crack Growth, NUREG/CP-0112, Vol. 1, pp. 299–306.
10.
Ford, F. P., and Andresen, P. L., 1990, “Corrosion Fatigue of A533B/A508 Pressure Vessel Steels in 288°C Water,” ibid., Vol. 1, pp. 105–124.
11.
Ha¨nninen
H.
,
To¨rro¨nen
K.
,
Kemppainen
M.
, and
Salonen
S.
,
1983
, “
On the Mechanisms of Environment Sensitive Cyclic Crack Growth of Nuclear Pressure Vessel Steels
,”
Corrosion Science
, Vol.
23
, No.
6
, pp.
663
679
.
12.
Hurst, P., Banks, P., Pemberton, G., and Raffel, A. S., 1986, “Stress Corrosion Behaviour of A533-B and A508-III Steels and Weldments in High Temperature Water Environments,” Proceedings, Second Symposium on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, American Nuclear Society, pp. 645–655.
13.
James
L. A.
,
1994
, “
The Effect of Temperature and Cyclic Frequency Upon Fatigue Crack Growth Behavior of Several Steels in an Elevated Temperature Aqueous Environment
,”
ASME JOURNAL OF PRESSURE VESSEL TECHNOLOGY
, Vol.
116
, pp.
122
127
.
14.
James
L. A.
, and
Wilson
W. K.
,
1994
, “
Development of a Surface-Cracked Specimen
,”
Theoretical and Applied Fracture Mechanics
, Vol.
20
, No.
2
, pp.
115
121
.
15.
Kitigawa, H., Komai, K., Nakajima, H., and Higuchi, M., 1987, “Testing Round Robin on Cyclic Crack Growth of Low and Medium Sulfur A533-B Steels in LWR Environments,” Trans. Ninth International Conference on Structural Mechanics in Reactor Technology, Vol. F, pp. 155–160.
16.
Kondo, T., Kikuyama, T., Nakajima, H., and Shindo, M., 1972, “Fatigue of Low-Alloy Steels in Aqueous Environment at Elevated Temperatures,” Mechanical Behavior of Materials, Proceedings of International Conference on Mechanical Behavior of Materials, Vol. 3, pp. 317–327.
17.
Lenz, E., Wieling, N., and Mu¨nster, H., 1988, “Influence of Variation of Flow Rates and Temperature on the Cyclic Crack Growth Rate Under BWR Conditions,” Proceedings, Third International Symposium on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, Met. Soc. of AIME, pp. 283–288.
18.
Macdonald
D. D.
,
Scott
A. C.
, and
Wentrcek
P.
,
1979
, “
Silver-Silver Chloride Thermocells and Thermal Liquid Junction Potentials for Potassium Chloride Solutions at Elevated Temperatures
,”
Journal of the Electrochemical Society
, Vol.
126
, No.
9
, pp.
1618
1624
.
19.
Macdonald
D. D.
,
Song
H.
,
Makela
K.
, and
Yoshida
K.
,
1993
, “
Corrosion Potential Measurements on Type 304 SS and Alloy 182 in Simulated BWR Environments
,”
Corrosion
, Vol.
49
, No.
1
, pp.
8
16
.
20.
Newman, J. C., and Raju, I. S., 1979, “Analysis of Surface Cracks in Finite Plates Under Tension or Bending Loads,” NASA Technical Paper 1578.
21.
Psaila-Dombrowski, M. J., 1990, “Modeling of Crack and Crevice Chemistry in Light Water Reactor Environments,” Ph.D. dissertation, Dept. of Nuclear Engineering, Massachusetts Institute of Technology, Cambridge, MA.
22.
Scott, P. M., and Truswell, A. E., 1981, “The Influence of Water Chemistry on Fatigue Crack Propagation in LWR Pressure Vessel Steels,” Proceedings of the International Atomic Energy Agency Specialists’ Meeting on Subcritical Crack Growth, NUREG/CP-0044, Vol. 2, pp. 91–126.
23.
Scott
P. M.
, and
Truswell
A. E.
,
1983
, “
Corrosion Fatigue Crack Growth in Reactor Pressure Vessel Steels in PWR Primary Water
,”
ASME JOURNAL OF PRESSURE VESSEL TECHNOLOGY
, Vol.
105
, pp.
245
254
.
24.
Scott
P. M.
,
Truswell
A. E.
, and
Druce
S. G.
,
1984
, “
Corrosion Fatigue of Pressure Vessel Steels in PWR Environments—Influence of Steel Sulfur Content
,”
Corrosion
, Vol.
40
, No.
7
, pp.
350
357
.
25.
Shack, W. J., et al, 1989, “Environmentally Assisted Cracking in Light Water Reactors,” NUREG/CR-4667, Vol. 5.
26.
Shoji
T.
,
Takahashi
H.
,
Suzuki
M.
, and
Kondo
T.
,
1981
, “
A New Parameter for Characterizing Corrosion Fatigue Crack Growth
,”
ASME Journal of Engineering Materials and Technology
, Vol.
103
, No.
4
, pp.
298
304
.
27.
Shoji, T., Takahashi, H., Nakajima, H., and Kondo, T., 1983, “Role of Loading Variables in Environment Enhanced Crack Growth for Water-Cooled Nuclear Reactor Pressure Vessel Steels,” Proceedings of International Atomic Energy Agency Specialists’ Meeting on Subcritical Crack Growth, NUREG/CP-0044, Vol. 2, pp. 143–171.
28.
Swan, D. I., and Chapman, O. J. V., 1990, “Modeling of Sulfide Inclusion Distributions in relation to the Environmentally Assisted Cracking of Low-Alloy Steels in a Pressurized Water Reactor Environment,” Environmentally Assisted Cracking: Science and Engineering, ASTM STP 1049, pp. 283–299.
29.
Tice
D. R.
,
1986
, “
Influence of Mechanical and Environmental Variables on Crack Growth in PWR Pressure Vessels
,”
International Journal of Pressure Vessels and Piping
, Vol.
24
, No.
2
, pp.
139
173
.
30.
To¨rro¨nen, K., Kemppainen, M., and Ha¨nninen, H., 1984, “Fractographic Evaluation of Specimens of A533 B Pressure Vessel Steel,” EPRI NP-3483.
31.
VanDerSluys, W. A., and Emanuelson, R. H., 1993, “Environmental Acceleration of Fatigue Crack Growth in Reactor Pressure Vessel Materials,” EPRI TR-102796, Vol. 1.
32.
Varfolomeyev
I. V.
,
Vainshtok
V. A.
, and
Krasowsky
A. Y.
,
1991
, “
Prediction of Part-Through Crack Growth Under Cyclic Loading
,”
Engineering Fracture Mechanics
, Vol.
40
, No.
6
, pp.
1007
1022
.
This content is only available via PDF.
You do not currently have access to this content.