A methodology for characterizing and assessing the behavior of materials after service in the creep range has been developed and used on a broad range of materials and components. It incorporates the results of relatively short-term tests and improved databases on materials properties. The essence of the method is the definition of a material performance characteristic which the author refers to by the symbol Ωp. This coefficient effectively describes the rate at which a material’s ability to resist stress is degraded by strain. While Ωp is a function of stress, temperature, and mode of loading, it is amenable to parametric representation and is, therefore, useful in predicting life and strain accumulation. Time to failure and total accumulated strain are shown to be consequences of a characterizing strain rate, as defined herein, and an appropriate Ωp for the operating conditions and geometry of interest. Accumulated strain, future strain, current creep rate, remaining life, total damage, and damage rate are among the quantities which are easily calculated. The development of the method employs and extends the concepts of Larson-Miller, Monkman-Grant, Robinson, Theta Projection, Kachanov, and Norton.

1.
American Petroleum Institute, 1988, API RP 530, Recommended Practice for Calculation of Heater Tube Thickness in Petroleum Refineries, Third Edition.
2.
Buchheim, G. M., Osage, D. A., Brown, R. G., and Dobis, J. D., 1994, “Failure Investigation of a Low-Chrome Long-Seam Investigation of a Low-Chrome Long-Seam Weld in a High-Temperature Refinery Piping System,” Service Experience and Reliability Improvement: Nuclear, Fossil and Petrochemical Plants, ASME Pressure Vessel and Piping Conference, Vol. 288.
3.
Evans, R. W., Parker, J. D., and Wilshire, B., 1982, “An Extrapolative Procedure for Long Term Creep Strain and Creep-Life Prediction,” Recent Advances in Creep and Fracture of Engineering Materials and Structures, Pine Ridge Press, pp. 135–184.
4.
Goldhoff, R. M., and Woodford, D. A., 1972, The Evaluation of Creep Damage in CrMoV Steel Testing for Prediction of Material Performance in Structures and Components, STP 515, American Society for Testing and Materials, Philadelphia, PA, pp. 89–106.
5.
Hart
R. V.
,
1976
, “
Assessment of Remaining Creep Life Using Accelerated Stress-Rupture Tests
,”
Metallurgical Technology
, Vol.
13
, p.
1
1
.
6.
Ibarra, S., and Konet, R. R., 1994, “Life Assessment of 1 1/4Cr-1/2Mo Steel Catalytic Reformer Furnace Tubes using the MPC Omega Method,” Service Experience and Reliability Improvement: Nuclear, Fossil and Petrochemical Plants, ASME Pressure Vessel and Piping Conference, Vol. 288.
7.
Kachanov
L. H.
,
1958
, IZV,
Akad. Nauk.
, USSR, Vol.
8
, p.
26
26
.
8.
Kawasaki
T.
, and
Horiguchi
M.
,
1979
, “
Analysis of Accelerated Creep Under Constant Sustaining Load Austenitic Stainless Steels
,”
Metallurgical Transactions A
, June, Vol.
10A
, pp.
749
757
.
9.
Klehn, R., and Laughlin, C. A. B., 1994, “CHEVRON’s Experience Using Omega Method Creep Tests for Life Assessment of Refinery Equipment,” Service Experience and Reliability Improvement: Nuclear, Fossil and Petrochemical Plants, ASME Pressure Vessel and Piping Conference, Vol. 288.
10.
Kussmaul, K., Malle, K., and Sheng, S., 1993, “A Damage-Based Strength Hypothesis for Multiaxial Loading in the Creep Range,” ASME PVP-Vol. 266, Creep, Fatigue, Evaluation and Leak-Before-Break Assessment, New York, NY.
11.
Leckie, F. A., 1985, “Damage Studies in Pressure Vessel Components,” WRC Bulletin 310, Welding Research Council, New York, NY, Dec.
12.
McLaughlin, J. E., Karcher, G. E., and Barnes, P., 1994, “Life Assessment of Carbon Steel Vessel with Cracks Operating in the Creep Range,” Service Experience and Reliability Improvement: Nuclear, Fossil and Petrochemical Plants, ASME Pressure Vessel and Piping Conference, Vol. 288.
13.
Monkman, F. C., and Grant, N. J., 1956, Proceedings, ASTM 56, p. 595.
14.
Neubauer, B., and Wedel, U., 1983, “Restlife Estimation of Creeping Components by Means of Replicas,” Advances in Life Prediction Methods, eds., D. A. Woodford and J. R. Whitehead, ASME, New York, NY, pp. 307–314.
15.
Prager, M., 1994 “The Omega Method—An Effective Method for Life and Damage Prediction in Creep Tests and Service,” presented at IC-SMA 10, Sendai, Japan, August 21–26.
16.
Prager, M., and Masuyama, F., 1994, “Examination of the Effects of Materials Variables in Advanced Alloys by Studying Creep Deformation Behavior,” presented at ICSMA 10, Sendai, Japan, August 21–26.
17.
Robinson
E. L.
,
1938
, “
Effects of Temperature Variation on the Creep Strength of Steels
,”
TRANS. ASME
, Vol.
160
, pp.
253
259
.
18.
Sandstrom, R., and Kondyr, A., 1979, “Model for Tertiary-Creep in Mo and Cr-Mo Steels,” ICM 3, Vol. 2, Cambridge, UK, Aug., pp. 275–284.
19.
Viswanathan, R., 1989, “Damage Mechanisms and Life Assessment of High Temperature Components,” ASM, p. 216.
This content is only available via PDF.
You do not currently have access to this content.