The austenitic steel 15-15Ti is being considered as one of the candidate materials for internal structural components of future heavy liquid metal (HLM) nuclear systems. This work studies the steel compatibility with liquid PbBi. Constant extension rate tensile (CERT) tests of tapered specimens were used to study sensitivity to liquid metal embrittlement (LME) and crack initiation. The taper creates a variation of stress along the gauge length which allows the identification of the stress and strain for the crack appearance. Testing was performed in air and in PbBi with 10−6 to 10−12 wt  % oxygen content at 300 °C. Post-test observation by scanning electron microscopy (SEM) highlighted the crack morphology. An evaluation of the environmental effect on the crack initiation is presented.

Issue Section:
Special Section on Research Center Řež: Nuclear-Engineering Activities in 2018
Keywords:
heavy liquid metals, generation IV nuclear systems, austenitic stainless steel, environmentally assisted cracking, liquid metal embrittlement, PbBi
Topics:
Fracture (Materials), Polishing, Stress, Steel

Reference

1.
Delville
,
R.
,
Stergar
,
E.
, and
Verwerft
,
M.
,
2014
, “
Results of a New Production of Nuclear-Grade 1.4970 ‘15-15TI’ Stainless Steel Fuel Cladding Tubes for Gen IV Reactors
,”
ASME
Paper No. ICONE22-30781.
2.
Yu
,
J.
,
Xue
,
L. J.
,
Zhao
,
Z. J.
,
Chi
,
G. X.
, and
Parkins
,
R. N.
,
1989
, “
Determination of Stress Corrosion Crack Initiation Stress and Crack Velocities Using Slowly Strained Tapered Specimens
,”
Fatigue Fract. Eng. Mater. Struct.
,
12
(
6
), pp.
481
–
493
.
Google Scholar
Crossref
Search ADS
 
3.
Berger
,
S.
,
Kilian
,
R.
,
Ritter
,
S.
,
Ehrnstén
,
U.
,
Bosch
,
R.-W.
, and
Perosanz Lopez
,
F.-J.
,
2016
, “
Mitigation of Crack Initiation in LWRs (MICRIN+)
,”
EUROCORR2016
, Montpellier, France, Sept. 11–15, Paper No. 65952.
4.
Ritter
,
S.
,
Kilian
,
R.
,
Herbst
,
M.
,
Bosch
,
R. W.
,
Burke
,
G.
,
Dinu
,
A.
,
Ehrnstén
,
U.
,
Hojná
,
A.
,
Martin
,
O.
,
Novotny
,
R.
,
Perosanz
,
F. J.
, and
Zajec
,
B.
,
2018
, “
Accelerated Testing of Stress Corrosion Cracking Initiation in High-Temperature Water—Results From the MICRIN Collaborative Project
,”
EUROCORR 2018
, Krakow, Poland, Sept. 9–13, Paper No. 119012.
5.
Lambrinou
,
K.
,
Gavrilov
,
S.
,
Van den Bosch
,
J.
,
Schroer
,
C.
, and
Tsisar
,
V.
,
2015
, “
Experimental Results in Flowing LBE
,” Matter Project Report, Deliverable D3.6–Part C, EURATOM FP7 Grant Agreement No. 26970.
6.
Van den Bosch
,
J.
,
2008
, “
ADS Candidate Materials Compatibility With Liquid Metal in a Neutron Irradiation Environment
,”
Ph.D. dissertation
, Ghent University, Ghent, Belgium.http://hdl.handle.net/1854/LU-671250
7.
Gorse
,
D.
,
Auger
,
T.
,
Vogt
,
J.-B.
,
Proriol Serre
,
I.
,
Weisenburger
,
A.
,
Gessi
,
A.
,
Agostini
,
P.
,
Fazio
,
C.
,
Hojna
,
A.
,
Di Gabriele
,
F.
,
Van Den Bosch
,
J.
,
Coen
,
G.
, and
Almazouzi
,
A.
,
2011
, “
Influence of Liquid Lead and Lead–Bismuth Eutectic on Tensile, Fatigue and Creep Properties of Ferritic/Martensitic and Austenitic Steels for Transmutation Systems
,”
J. Nucl. Mater.
,
415
(
3
), pp.
284
–
292
.
Google Scholar
Crossref
Search ADS
 
8.
Coen
,
G.
,
Van den Bosch
,
J.
,
Almazouzi
,
A.
, and
Degrieck
,
J.
,
2010
, “
Investigation of the Effect of Lead–Bismuth Eutectic on the Fracture Properties of T91 and 316 L
,”
J. Nucl. Mater.
,
398
(
1–3
), pp.
122
–
128
.
Google Scholar
Crossref
Search ADS
 
Copyright © 2019 by ASME
You do not currently have access to this content.