Generally, fatigue strength of steel correlates with hardness up to a certain point. However, the relationship of hardness and fatigue strength is more complicated for high strength materials, mainly because strength is sensitive to material defects. This paper presents a determination of defect size in carburized gear teeth and a strength evaluation method based on that size. A micro notch is artificially processed at the fillet of carburized gear tooth by means of a Focused Ion Beam, and a bending fatigue test is performed. Threshold notch depth the limit beyond which fatigue strength declines, is obtained by the test. Threshold notch depth is used as a measure to determine latent defect size in the surface layer. The of gears from which a nonmartensitic layer is removed by electro-polishing is shorter than the of gears with a nonmartensitic layer. The surface layer is observed by scanning electron microscope and electron probe micro analyzer to clarify latent defect characteristics. Many micro cracks, in addition to long cracks in the nonmartensitic layer, Cr oxides and Mn oxides near the surface, and Si segregated in grain boundary are observed. This demonstrates that they trigger fatigue crack initiation; and therefore defect size limits strength. Consequently, strength is expressed by an experimental formula of Vickers hardness and the square root of projected area of the defect obtained above.
Skip Nav Destination
Article navigation
September 2002
Technical Papers
Evaluation of Bending Strength of Carburized Gears Based on a Quantification of Defect Size in the Surface Layer
Tomoya Masuyama,
Tomoya Masuyama
Research Assistant, Department of Machine Intelligence and Systems Engineering, Tohoku University, Sendai 980-8579, Japan
Search for other works by this author on:
Masana Kato, Professor,,
Masana Kato, Professor,
Department of Machine Intelligence and Systems Engineering, Akita Prefectural University, Honjo 015-0055, Japan
Search for other works by this author on:
Katsumi Inoue, Professor,,
Katsumi Inoue, Professor,
Department of Machine Intelligence and Systems Engineering, Tohoku University, Sendai 980-8579, Japan
Search for other works by this author on:
Toshihiko Yamashita
Toshihiko Yamashita
Electronic Controls Division, Yamaha Motor Co., Ltd., Iwata 438-8501, Japan
Search for other works by this author on:
Tomoya Masuyama
Research Assistant, Department of Machine Intelligence and Systems Engineering, Tohoku University, Sendai 980-8579, Japan
Masana Kato, Professor,
Department of Machine Intelligence and Systems Engineering, Akita Prefectural University, Honjo 015-0055, Japan
Katsumi Inoue, Professor,
Department of Machine Intelligence and Systems Engineering, Tohoku University, Sendai 980-8579, Japan
Toshihiko Yamashita
Electronic Controls Division, Yamaha Motor Co., Ltd., Iwata 438-8501, Japan
Contributed by the Power Transmission and Gearing Committee for publication in the JOURNAL OF MECHANICAL DESIGN. Manuscript received December 2000. Associate Editor: R. F. Handschuh.
J. Mech. Des. Sep 2002, 124(3): 533-538 (6 pages)
Published Online: August 6, 2002
Article history
Received:
December 1, 2000
Online:
August 6, 2002
Citation
Masuyama, T., Kato, M., Inoue, K., and Yamashita, T. (August 6, 2002). "Evaluation of Bending Strength of Carburized Gears Based on a Quantification of Defect Size in the Surface Layer ." ASME. J. Mech. Des. September 2002; 124(3): 533–538. https://doi.org/10.1115/1.1485091
Download citation file:
Get Email Alerts
Cited By
Multi-Split Configuration Design for Fluid-Based Thermal Management Systems
J. Mech. Des (February 2025)
Related Articles
Analysis of Variable Amplitude Fatigue Data of the P355NL1 Steel Using the Effective Strain Damage Model
J. Pressure Vessel Technol (October,2009)
An Experimental Investigation of Bending Fatigue Initiation and Propagation Lives
J. Mech. Des (September,2001)
Proposed New Fatigue Design Curves for Carbon and Low-Alloy Steels in
High Temperature Water
J. Pressure Vessel Technol (April,2009)
On the Characterization of Fatigue Crack Growth in a Plate With a Single-Sided Repair
J. Eng. Mater. Technol (April,2004)
Related Proceedings Papers
Related Chapters
Development of New Process and Product Monitoring Technologies for the Manufacturing of High Value Alloy Steels for Use in Critical Applications
Bearing and Transmission Steels Technology
In Situ Observations of the Failure Mechanisms of Hydrided Zircaloy-4
Zirconium in the Nuclear Industry: 20th International Symposium
Fatigue Crack Growth, Fatigue, and Stress Corrosion Crack Growth: Section XI Evaluation
Online Companion Guide to the ASME Boiler & Pressure Vessel Codes