The fracture toughness of highly-ordered multi-wall carbon-nanotube-reinforced alumina composites is calculated from experimental data on nanoindentation cracking. A combined analytical and numerical model, using cohesive zone models for both matrix cracking and nanotube crack bridging and accounting for residual stresses, is developed to interpret the indentation results and evaluate the fracture toughness of the composite. Results show that residual stress and nanotube bridging play important roles in the nanocomposite fracture. The contribution to toughness from the nanotube bridging for cracking transverse to the axis of the nanotubes is calculated to be ∼5 MPa-m1/2. From the nanotube bridging law, the nanotube strength and interfacial frictional stress are also estimated and range from 15–25 GPa and 40–200 MPa, respectively. These preliminary results demonstrate that nanotube-reinforced ceramics can exhibit the interfacial debonding/sliding and nanotube bridging necessary to induce nanoscale toughening, and suggest the feasibility of engineering residual stresses, nanotube structure, and composite geometry to obtain high-toughness nanocomposites.
Skip Nav Destination
Article navigation
July 2004
Technical Papers
Fracture Toughness of Highly Ordered Carbon Nanotube/Alumina Nanocomposites
Z. Xia,
Z. Xia
Division of Engineering, Brown University, Providence, Rhode Island, 02912
Search for other works by this author on:
W. A. Curtin,
W. A. Curtin
Division of Engineering, Brown University, Providence, Rhode Island, 02912
Search for other works by this author on:
B. W. Sheldon
B. W. Sheldon
Division of Engineering, Brown University, Providence, Rhode Island, 02912
Search for other works by this author on:
Z. Xia
Division of Engineering, Brown University, Providence, Rhode Island, 02912
W. A. Curtin
Division of Engineering, Brown University, Providence, Rhode Island, 02912
B. W. Sheldon
Division of Engineering, Brown University, Providence, Rhode Island, 02912
Contributed by the Materials Division for publication in the JOURNAL OF ENGINEERING MATERIALS AND TECHNOLOGY. Manuscript received by the Materials Division July 30, 2003; revision received March 1, 2004. Associate Editor: Y. Huang.
J. Eng. Mater. Technol. Jul 2004, 126(3): 238-244 (7 pages)
Published Online: June 29, 2004
Article history
Received:
July 30, 2003
Revised:
March 1, 2004
Online:
June 29, 2004
Citation
Xia , Z., Curtin , W. A., and Sheldon, B. W. (June 29, 2004). "Fracture Toughness of Highly Ordered Carbon Nanotube/Alumina Nanocomposites ." ASME. J. Eng. Mater. Technol. July 2004; 126(3): 238–244. https://doi.org/10.1115/1.1751179
Download citation file:
Get Email Alerts
Modeling Growth and Viscous Flow of Oxide on Cylindrical Silicon Surfaces Including Piezoviscous Inhibition
J. Eng. Mater. Technol (April 2025)
Thermal Conductivity of 3D-Printed Metal Using Extrusion-Based Metal Additive Manufacturing Process
J. Eng. Mater. Technol (April 2025)
Related Articles
Recent Developments in Multifunctional Nanocomposites Using Carbon Nanotubes
Appl. Mech. Rev (September,2010)
Fracture Toughness of Composite Joints With Carbon Nanotube Reinforcement
J. Pressure Vessel Technol (April,2011)
Mechanical Characterization of XD-Grade Carbon Nanotube/Epon 862 Processed by Dual Phase Dispersion Technique
J. Eng. Mater. Technol (October,2011)
A Micromechanics Model for the Thermal Conductivity of Nanotube-Polymer Nanocomposites
J. Appl. Mech (July,2008)
Related Proceedings Papers
Related Chapters
Characterization of Ultra-High Temperature and Polymorphic Ceramics
Advanced Multifunctional Lightweight Aerostructures: Design, Development, and Implementation
Layer Arrangement Impact on the Electromechanical Performance of a Five-Layer Multifunctional Smart Sandwich Plate
Advanced Multifunctional Lightweight Aerostructures: Design, Development, and Implementation
Preparation and Thermal Property of Phase Change Nanocomposites Using Carbon Nanotubes as Additives
Inaugural US-EU-China Thermophysics Conference-Renewable Energy 2009 (UECTC 2009 Proceedings)