This paper investigates the damage development in SiC/SiNC woven composites under tensile and cyclic loading both at room and elevated temperatures. The ultimate strength, failure strain, proportional limit, and modulus data at a temperature range of 23°C–1250°C are generated. The tensile strength of SiC/SiNC woven composites has been observed to increase with increased temperatures up to 1000°C. The stress/strain plot shows a pseudo-yield point at 25 percent of the failure strain $εf,$ which indicates damage initiation in the form of matrix cracking. The evolution of damage above 0.25 $εf$ both at room and elevated temperature comprises of multiple matrix cracking, interfacial debonding, and fiber pullout. Although the nature of the stress/strain plot shows damage-tolerant behavior under static loading both at room and elevated temperature, the life expectancy of SiC/SiNC composites degrades significantly under cyclic loading at elevated temperature. This is mostly due to the interactions of fatigue damage caused by the mechanically induced plastic strain and the damage developed by the creep strain. The in-situ damage evolutions are monitored by acoustic event parameters, ultrasonic C-scan, and stiffness degradation. Rate equations for modulus degradation and fatigue life prediction of ceramic matrix composites both at room and elevated temperatures are developed. These rate equations are observed to show reasonable agreement with experimental results. [S0094-4289(00)02304-5]

1.
Levine, S. R., 1992, “Flight-Vehicle Materials, Structures, and Dynamics—Assessment and Future Directions,” Vol. 3, ASME, pp. 1–17.
2.
Yen, C. F., and Jones, M. L., 1997, “Material Modeling for Cross-Ply Ceramic Matrix Laminates with Progressive Damages and Environmental Degradation,” MD-Vol.80, Composites and Functionally Graded Materials, ASME, pp. 189–202.
3.
Talreja, R., 1990, “Fatigue of Fiber-Reinforced Ceramics,” Structural Ceramics-Processing, Microstructure and Properties,” Proceedings of the 11th Rise International Symposium on Metallurgy and Materials Science, pp. 145–159.
4.
Pastor, M. S., Case, S. W., and Reifsnider, K. L., 1998, “Durability of Ceramic Matrix Composites,” AD-Vol.56, Recent Advances in Mechanics and Aerospace Structures and Materials, pp. 61–66.
5.
Burr, A., Hild, F., and Leckie, F. A., 1997, “Damage, Fatigue, and Failure of Ceramic-Matrix Composites,” Applications of Continuum Damage Mechanics to Fatigue and Fracture, ASTM STP 1315, McDowell, D. L., ed., American Society for Testing and Materials, pp. 83–96.
6.
Holmes
,
J. W.
,
1991
, “
Tensile Creep Behavior of a Fiber Reinforced SiC/Si3N4 Composites
,”
J. Mater. Sci.
,
26
, pp.
1808
1814
.
7.
Weibelzahl
,
W.
,
Mutz
,
G.
,
Suttor
,
D.
, and
Ziegler
,
G.
,
1999
, “
Corrosion Stability and Mechanical Properties of Polysilazane—Derived SiCN—Ceramics
,”
Key Eng. Mater.
,
161–163
, pp.
111
114
.
8.
Mahfuz, H., Eltom, K., Das, P. S., Vaidya, U., Sodah, S., and Jeelani, S., 1997, “High Frequency Fatigue of Continuous Silicon Carbide Fiber Reinforced Silicon Nitride SiC/Si3N4 Matrix Composites,” 29th International SAMPE Technical Conference, pp. 128–141.
You do not currently have access to this content.