Abstract
The effects of temperature variation on microstructural evolution were investigated for Cu, Cu-5Ni, Cu-3.5Zn, and Cu-5Ni-2Zn irradiated in JMTR and HFIR. The low temperature pre-irradiation at 477 K to 533 K was shown not to influence microstructural evolution significantly during the following irradiation at 613 K to 693 K. On the other hand, downward temperature shift during irradiation was shown to produce void formation in Cu and Cu-3.5Zn. The mechanism of the temperature variation effects was discussed based on the defect properties and the details of the temperature transient history during irradiation.
Issue Section:
Research Papers
References
1.
Muroga
, T.
, Zinkle
, S. J.
, Qualls
, A. L.
, Watanabe
, H.
, “Varying Temperature Irradiation Experiment in HFIR
,” Journal of Nuclear Materials
0022-3115, Vol. 299
, 2001
, pp. 148
-156
.2.
Watanabe
, H.
, Muroga
, T.
, and Yoshida
, N.
, “Effects of Varying Temperature Irradiation on the Microstructure of Neutron Irradiated Austenitic Stainless Steels
,” Proceedings of the Fourth Pacific Rim International Conference on Advanced Materials and Processing (PRICM4)
, S.
Hanada
, Z.
Zhong
, S. W.
Nam
, and R. N.
Wright
, Eds., The Japan Institute of Metals
, Sendai
, 2001
, pp. 1315
-1317
.3.
Zinkle
, S. J.
, Hashimoto
, N.
, Hoelzer
, D. T.
, Qualls
, A. L.
, Muroga
, T.
, and Singh
, B. N.
, “Effect of Periodic Temperature Variations on the Microstructure of Neutron Irradiated Metals
,” Journal of Nuclear Materials
0022-3115, Vols. 307–311
, 2002
, pp. 192
-196
.4.
Watanabe
, H.
, Muroga
, T.
, and Yoshida
, N.
, “Effects of Temperature Variation on Vanadium Alloys Irradiated in HFIR
,” Journal of Nuclear Materials
0022-3115, Vols. 307–311
, 2002
, pp. 403
-407
.5.
Kiritani
, M.
, Endoh
, T.
, Hamada
, K.
, Yoshiie
, T.
, Okada
, A.
, Kojima
, S.
, et al, “Fission Reactor Irradiation of Materials with Improved Control of Neutron Flux-Temperature History
,” Journal of Nuclear Materials
0022-3115, Vols. 179–181
, 1991
, pp. 1104
-1107
.6.
Kiritani
, M.
, Yoshiie
, T.
, Iseki
, M.
, Kojima
, S.
, Hamada
, K.
, Horiki
, M.
, et al, “Microstructure Evolution by Neutron Irradiation During Cyclic Temperature Variation
,” Journal of Nuclear Materials
0022-3115, Vols. 212–215
, 1994
, pp. 241
-245
.7.
Muroga
, T.
, Ishimaru
, E.
, and Yoshida
, N.
, “The Role of Nickel and Zinc in Defect Behavior and Microstructural Evolution of Copper under Electron Irradiation
,” Effects of Radiation on Materials: 16th Conference
, ASTM STP 1175, A. S.
Kumar
, D. S.
Gelles
, R. K.
Nanstad
, and E. A.
Little
, Eds., ASTM International
, West Conshohocken, PA
, 1993
, pp. 1013
-1025
.8.
Muroga
, T.
, Matsue
, T.
, Watanabe
, H.
, and Yoshida
, N.
, “Void Swelling of Copper and Copper Alloys Induced by Heavy Ion Irradiation
,” Effects of Radiation on Materials: 18th International Symposium
, ASTM STP 1325, R. K.
Nanstad
, M. L.
Hamilton
, F. A.
Garner
, and A. S.
Kumar
, Eds., ASTM International
, West Conshohocken, PA
, 1999
, pp. 991
-998
.9.
Muroga
, T.
and Yoshida
, N.
, “Microstructure of Neutron-Irradiated Copper Alloyed with Nickel and Zinc
,” Journal of Nuclear Materials
0022-3115, Vols. 212–215
, 1994
, pp. 266
-269
.10.
Xu
, Q.
, Heinisch
, H. L.
, and Yoshiie
, T.
, “Computer Simulation of the Effect of Temperature Change on Defect Accumulation in Copper During Neutron Irradiation
,” Journal of Nuclear Materials
0022-3115, Vols. 283–287
, 2000
, pp. 297
-301
.11.
Singh
, B. N.
and Zinkle
, S. J.
, “Defect Accumulation in Pure FCC Metals in the Transient Regime: A Review
,” Journal of Nuclear Materials
0022-3115 https://doi.org/10.1016/0022-3115(93)90125-I, Vol. 206
, 1993
, pp. 212
-229
.12.
Nita
, N.
, Iwai
, T.
, Fukumoto
, K.
, and Matsui
, H.
, “Effects of Temperature Change on the Microstructural Evolution of Vanadium Alloys under Ion Irradiation
,” Journal of Nuclear Materials
0022-3115, Vols. 283–287
, 2000
, pp. 291
-295
.
This content is only available via PDF.
All rights reserved. This material may not be reproduced or copied, in whole or in part, in any printed, mechanical, electronic, film, or other distribution and storage media, without the written consent of ASTM International.
You do not currently have access to this content.