This study examines damage initiation and propagation in solder joints with voids, under thermomechanical cyclic loading. An accelerated thermal cycling test is conducted on printed wiring assemblies (PWAs) containing 256 input/output (I/O) plastic ball grid arrays (PBGAs) with voided solder joints. Destructive and nondestructive failure analyses of the solder balls are used to detect the presence of voids and to relate the extent of damage propagation to the number of thermal cycles. Particular cases of voided and damaged joints are selected from these tests, to guide the development of a strategy for modeling damage propagation, using a three dimensional global-local finite element analysis (FEA). The displacement results of the global FEA at the top and bottom of the selected solder balls are used as the boundary conditions in a local FEA model, which focuses on the details of damage initiation and propagation in the individual solder ball. The local model is error seeded with voids based on cases selected in experiment. The damage propagation rate is monitored for all the cases. The technique used to quantify cyclic creep-fatigue damage is a continuum model based on energy partitioning. A method of successive initiation is used to model the growth and propagation of damage in the selected case studies. The modeling approach is qualitatively verified using the results of the accelerated thermal cycling test. The verified modeling technique described above is then used for parametric study of the durability of voided solder balls in a ChipArray Thin Core BGA with 132 I/O (CTBGA132) assemblies, under thermal cycling. The critical solder ball in the package is selected and is error seeded with voids with different sizes and various distances from damage initiation site. The results show that voids in general are not detrimental to thermal cycling durability of the CTBGA132 assembly, except when a large portion of the damage propagation path is covered with voids. Small voids can arrest the damage propagation, but generally do not provide a significant increase in durability because the damage zone deflects around the void and also continues to propagate from other critical regions in the solder ball.
Skip Nav Destination
e-mail: ladani@engineering.usu.edu
Article navigation
March 2008
Research Papers
Damage Initiation and Propagation in Voided Joints: Modeling and Experiment
Leila Jannesari Ladani,
Leila Jannesari Ladani
Department of Mechanical and Aerospace Engineering,
e-mail: ladani@engineering.usu.edu
Utah State University
, Logan, UT 84341
Search for other works by this author on:
Abhijit Dasgupta
Abhijit Dasgupta
Department of Mechanical Engineering,
University of Maryland
, College Park, MD 20742
Search for other works by this author on:
Leila Jannesari Ladani
Department of Mechanical and Aerospace Engineering,
Utah State University
, Logan, UT 84341e-mail: ladani@engineering.usu.edu
Abhijit Dasgupta
Department of Mechanical Engineering,
University of Maryland
, College Park, MD 20742J. Electron. Packag. Mar 2008, 130(1): 011008 (11 pages)
Published Online: February 4, 2008
Article history
Received:
February 1, 2007
Revised:
August 29, 2007
Published:
February 4, 2008
Citation
Ladani, L. J., and Dasgupta, A. (February 4, 2008). "Damage Initiation and Propagation in Voided Joints: Modeling and Experiment." ASME. J. Electron. Packag. March 2008; 130(1): 011008. https://doi.org/10.1115/1.2837562
Download citation file:
Get Email Alerts
Impact of Encapsulated Phase Change Material Additives for Improved Thermal Performance of Silicone Gel Insulation
J. Electron. Packag (December 2024)
Special Issue on InterPACK2023
J. Electron. Packag
Extreme Drop Durability of Sintered Silver Traces Printed With Extrusion and Aerosol Jet Processes
J. Electron. Packag (December 2024)
Related Articles
Effect of Voids on Thermomechanical Durability of Pb-Free BGA Solder Joints: Modeling and Simulation
J. Electron. Packag (September,2007)
Failure Analysis of Miniature Solder Specimen
J. Electron. Packag (March,2004)
Systematic Study on Thermo-Mechanical Durability of Pb-Free Assemblies: Experiments and FE Analysis
J. Electron. Packag (December,2005)
Thermomechanical Durability of High I/O BGA Packages
J. Electron. Packag (September,2002)
Related Proceedings Papers
Related Chapters
Polycrystalline Simulations of In-Reactor Deformation of Zircaloy-4 Cladding Tubes during Nominal Operating Conditions
Zirconium in the Nuclear Industry: 20th International Symposium
Surface Analysis and Tools
Tribology of Mechanical Systems: A Guide to Present and Future Technologies
Advanced PWR Cladding Development through Extensive In-Reactor Testing
Zirconium in the Nuclear Industry: 20th International Symposium