The effect of constant temperature and humidity environments on the durability of interconnects in underfilled Flip-Chip-on-Board (FCOB) assemblies is investigated in this study. Polymeric underfills, used to enhance thermomechanical durability of the interconnects, are found to create new failure modes due to hygromechanical swelling. Based on experimental observations, the failure mechanism is hypothesized to be cracking of intermetallics, which have weakened due to thermal aging. Pseudo 3-D finite element analyses are conducted to quantify the moisture absorption and diffusion through the polymeric underfill, and the resulting hygromechanical viscoplastic stress history. The simulations are combined with accelerated aging tests to assess in-service durability in hot, humid environments. Model predictions are compared with results of accelerated life tests available in the literature.
Hygro-Mechanical Durability of Underfilled Flip-Chip-on-Board (FCOB) Interconnects
Contributed by the Electronic and Photonic Packaging Division for publication in the JOURNAL OF ELECTRONIC PACKAGING. Manuscript received at ASME Headquarters August 22, 2001. Associate Editor: J. Lau.
- Views Icon Views
- Share Icon Share
- Cite Icon Cite
- Search Site
Okura, J. H., Dasgupta, A., and Caers, J. F. J. M. (July 26, 2002). "Hygro-Mechanical Durability of Underfilled Flip-Chip-on-Board (FCOB) Interconnects ." ASME. J. Electron. Packag. September 2002; 124(3): 184–187. https://doi.org/10.1115/1.1477193
Download citation file:
- Ris (Zotero)
- Reference Manager