Abstract

The ball-on-three-ball test method (B3B) is used to measure the flexural strength of cement paste and mortar. This method has the advantage of utilizing small and thin samples requiring less material and improved sensitivity, allowing a large number of samples to be tested for improved variability assessment, and assessing chemical degradation rapidly because of its relatively high surface-to-volume ratio. This paper examines two specific questions that have surfaced with the recent adoption of this test method in ASTM C1904-20, Standard Test Methods for Determination of the Effects of Biogenic Acidification on Concrete Antimicrobial Additives and/or Concrete Products. The first question is whether the mixing technique used in sample preparation impacts the results. It was found that the use of vacuum mixing (ASTM C1904-20) and Hobart mixing (ASTM C227-10, Standard Test Method for Potential Alkali Reactivity of Cement-Aggregate Combinations (Mortar-Bar Method), and ASTM C305-20, Standard Practice for Mechanical Mixing of Hydraulic Cement Pastes and Mortars of Plastic Consistency), provide comparable results; however, the high-shear mixing (ASTM C1738, Standard Practice for High-Shear Mixing of Hydraulic Cement Paste) indicated that the results were not statistically similar to the other mixing techniques. The second question is related to the timing of the test after the samples are removed from an exposure solution. It was found that the sample should be removed from the exposure solutions and tested within 10 minutes to maintain low variability. These results will provide information needed to evaluate changes for ASTM C1904-20.

References

1.
Popovics
S.
, “
13-Internal Structure of Concrete and Its Optimization
,” in
Concrete Materials
, 2nd ed., ed.
Popovics
S.
(
Oxford, UK
:
William Andrew Publishing
,
1992
),
475
511
, https://doi.org/10.1016/B978-0-8155-1308-7.50017-X
2.
MacGregor
J. G.
,
Reinforced Concrete: Mechanics and Design
(
Upper Saddle River, NJ
:
Prentice Hall
,
1997
).
3.
Mehta
P. K.
,
Concrete. Structure, Properties and Materials
(
Englewood Cliffs, NJ
:
Prentice-Hall, Incorporated
,
1986
).
4.
Standard Test Method for Splitting Tensile Strength of Cylindrical Concrete Specimens
, ASTM C496 (West Conshohocken, PA:
ASTM International
, approved October 1,
2017
), https://doi.org/10.1520/C0496_C0496M-17
5.
Standard Test Method for Flexural Strength of Concrete (Using Simple Beam with Third-Point Loading) (Superseded)
, ASTM C78/C78M-18 (West Conshohocken, PA:
ASTM International
, approved January 1,
2018
), https://doi.org/10.1520/C0078_C0078M-18
6.
Standard Test Method for Flexural Strength of Concrete (Using Simple Beam with Center-Point Loading)
, ASTM C293/C293M-16 (West Conshohocken, PA:
ASTM International
, approved April 15,
2016
), https://doi.org/10.1520/C0293_C0293M-16
7.
Standard Test Method for Flexural Strength of Hydraulic-Cement Mortars (Superseded)
, ASTM C348-20 (West Conshohocken, PA:
ASTM International
, approved April 1,
2020
), https://doi.org/10.1520/C0348-20
8.
Godfrey
D. J.
, “
Fabrication, Formulation, Mechanical Properties, and Oxidation of Sintered Si3N4 Ceramics Using Disc Specimens
,”
Materials Science and Technology
1
, no. 
7
(July
1985
):
510
515
, https://doi.org/10.1179/mst.1985.1.7.510
9.
Hulm
B. J.
,
Parker
J. D.
, and
Evans
W. J.
, “
Biaxial Strength of Advanced Materials
,”
Journal of Materials Science
33
, no. 
13
(July
1998
):
3255
3266
, https://doi.org/10.1023/A:1013216825960
10.
Wachtman
J. B.
,
Cannon
W. R.
, and
Matthewson
M. J.
,
Mechanical Properties of Ceramics
, 2nd ed. (
Hoboken, NJ
:
Wiley
,
2009
).
11.
Munz
D.
and
Fett
T.
,
Ceramics Mechanical Properties, Failure Behaviour, Materials Selection
, 1st ed. (
Berlin
:
Springer-Verlag Berlin Heidelberg
,
1999
).
12.
Shetty
D. K.
,
Rosenfield
A. R.
,
Duckworth
W. H.
, and
Held
P. R.
, “
A Biaxial-Flexure Test for Evaluating Ceramic Strengths
,”
Journal of the American Ceramic Society
66
, no. 
1
(January
1983
):
36
42
, https://doi.org/10.1111/j.1151-2916.1983.tb09964.x
13.
Börger
A.
,
Supancic
P.
, and
Danzer
R.
, “
The Ball on Three Balls Test for Strength Testing of Brittle Discs: Stress Distribution in the Disc
,”
Journal of the European Ceramic Society
22
, nos.
9–10
(September
2002
):
1425
1436
, https://doi.org/10.1016/S0955-2219(01)00458-7
14.
Börger
A.
,
Supancic
P.
, and
Danzer
R.
, “
The Ball on Three Balls Test for Strength Testing of Brittle Discs: Part II: Analysis of Possible Errors in the Strength Determination
,”
Journal of the European Ceramic Society
24
, nos. 
10–11
(September
2004
):
2917
2928
, https://doi.org/10.1016/j.jeurceramsoc.2003.10.035
15.
Nohut
S.
, “
A General Formulation for Strength Prediction of Advanced Ceramics by Ball-on-Three-Balls (B3B)-Test with Different Multiaxial Failure Criteria
,”
Ceramics International
38
, no. 
3
(April
2012
):
2411
2420
, https://doi.org/10.1016/j.ceramint.2011.11.007
16.
Temenoff
J. S.
and
Mikos
A. G.
,
Biomaterials: The Intersection of Biology and Materials Science
, 1st ed. (
Upper Saddle River, NJ
:
Pearson/Prentice Hall
,
2008
).
17.
Fu
T.
and
Weiss
W.
, “
The Ball-on-Three-Ball (B3B) Test–Application to Cement Paste and Mortar
,”
Advances in Civil Engineering Materials
9
, no. 
1
(March
2020
):
128
142
, https://doi.org/10.1520/ACEM20180070
18.
Erbektas
A. R.
,
Development of Practical Accelerated Testing Protocols for the Performance Evaluation of Concrete against Microbially Induced Corrosion of Concrete
(
Corvallis, OR
:
Oregon State University
,
2018
).
19.
Erbektas
A. R.
,
Isgor
O. B.
, and
Weiss
W.
, “
Comparison of Chemical and Biogenic Acid Attack on Concrete
,”
ACI Materials Journal
117
, no. 
1
: (January
2020
):
255
264
, https://doi.org/10.14359/51720293
20.
Cao
Y.
,
Zavaterri
P.
,
Youngblood
J.
,
Moon
R.
, and
Weiss
J.
, “
The Influence of Cellulose Nanocrystal Additions on the Performance of Cement Paste
,”
Cement and Concrete Composites
56
(February
2015
):
73
83
, https://doi.org/10.1016/j.cemconcomp.2014.11.008
21.
Cao
Y.
,
Zavattieri
P.
,
Youngblood
J.
,
Moon
R.
, and
Weiss
J.
, “
The Relationship between Cellulose Nanocrystal Dispersion and Strength
,”
Construction & Building Materials
119
(August
2016
):
71
79
, https://doi.org/10.1016/j.conbuildmat.2016.03.077
22.
Fu
T.
,
Montes
F.
,
Suraneni
P.
,
Youngblood
J.
, and
Weiss
J.
, “
The Influence of Cellulose Nanocrystals on the Hydration and Flexural Strength of Portland Cement Pastes
,”
Polymers
9
, no. 
9
(September
2017
): 424, https://doi.org/10.3390/polym9090424
23.
Qiao
C.
,
Suraneni
P.
, and
Weiss
J.
, “
Flexural Strength Reduction of Cement Pastes Exposed to CaCl2 Solutions
,”
Cement and Concrete Composites
86
(February
2018
):
297
305
, https://doi.org/10.1016/j.cemconcomp.2017.11.021
24.
Kim
J.
,
Yi
C.
, and
Zi
G.
, “
Biaxial Flexural Strength of Concrete by Two Different Methods
,”
Magazine of Concrete Research
64
, no. 
12
(December
2012
):
1057
1065
, https://doi.org/10.1680/macr.11.00178
25.
Cao
Y.
,
Weiss
W. J.
,
Youngblood
J.
,
Moon
R.
, and
Zavattieri
P.
, “
Performance-Enhanced Cementitious Materials by Cellulose Nanocrystal Additions
,” in
Production and Applications of Cellulose Nanomaterials
(
Peachtree Corners, GA
:
TAPPI Press
,
2013
),
135
136
.
26.
Qiao
C.
,
Suraneni
P.
, and
Weiss
J.
, “
Damage in Cement Pastes Exposed to NaCl Solutions
,”
Construction & Building Materials
171
(May
2018
):
120
127
, https://doi.org/10.1016/j.conbuildmat.2018.03.123
27.
Standard Test Method for Flexural Toughness of Fiber Reinforced Concrete (Using Centrally Loaded Round Panel)
, ASTM C1550-20 (West Conshohocken, PA:
ASTM International
, approved October 1,
2020
), https://doi.org/10.1520/C1550-20
28.
Standard Test Method for Compressive Strength of Cylindrical Concrete Specimens
(Superseded), ASTM C39-20 (West Conshohocken, PA:
ASTM International
, approved February 1,
2020
), https://doi.org/10.1520/C0039-20
29.
Standard Test Method for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insulating Materials by Four-Point Bending
, ASTM D6272-17 (West Conshohocken, PA:
ASTM International
, approved March 1,
2017
), https://doi.org/10.1520/D6272-17
30.
Konsta-Gdoutos
M. S.
,
Metaxa
Z. S.
, and
Shah
S. P.
, “
Multi-scale Mechanical and Fracture Characteristics and Early-Age Strain Capacity of High Performance Carbon Nanotube/Cement Nanocomposites
,”
Cement and Concrete Composites
32
, no. 
2
(February
2010
):
110
115
, https://doi.org/10.1016/j.cemconcomp.2009.10.007
31.
Konsta-Gdoutos
M. S.
,
Metaxa
Z. S.
, and
Shah
S. P.
, “
Highly Dispersed Carbon Nanotube Reinforced Cement Based Materials
,”
Cement and Concrete Research
40
, no. 
7
(July
2010
):
1052
1059
, https://doi.org/10.1016/j.cemconres.2010.02.015
32.
de With
G.
and
Wagemans
H. H. M.
, “
Ball-on-Ring Test Revisited
,”
Journal of the American Ceramic Society
72
, no. 
8
(August
1989
):
1538
1541
, https://doi.org/10.1111/j.1151-2916.1989.tb07702.x
33.
Erbektas
A. R.
,
Isgor
O. B.
, and
Weiss
W. J.
, “
An Accelerated Testing Protocol for Assessing Microbially Induced Concrete Deterioration during the Bacterial Attachment Phase
,”
Cement and Concrete Composites
104
(November
2019
): 103339, https://doi.org/10.1016/j.cemconcomp.2019.103339
34.
Stamoulis
K.
and
Giannakopoulos
A. E.
, “
Size Effects on Strength, Toughness and Fatigue Crack Growth of Gradient Elastic Solids
,”
International Journal of Solids and Structures
45
, nos.
18–19
(September
2008
):
4921
4935
, https://doi.org/10.1016/j.ijsolstr.2008.04.026
35.
Dönmez
A.
and
Bažant
Z. P.
, “
Size Effect on Punching Strength of Reinforced Concrete Slabs with and without Shear Reinforcement
,”
ACI Structural Journal
114
, no. 
4
(July
2017
):
875
866
, https://doi.org/10.14359/51689719
36.
Fessler
H.
and
Fricker
D. C.
, “
A Theoretical Analysis of the Ring‐on‐Ring Loading Disk Test
,”
Journal of the American Ceramic Society
67
, no. 
9
(September
1984
):
582
588
, https://doi.org/10.1111/j.1151-2916.1984.tb19598.x
37.
Shetty
D.
,
Rosenfield
A. R.
,
McGuire
P.
,
Bansal
G. K.
, and
Duckworth
W. H.
, “
Biaxial Flexure Tests for Ceramics
,”
American Ceramic Society Bulletin
59
, no. 
12
(December
1980
):
36
42
.
38.
Standard Specification for Portland Cement (Superseded)
, ASTM C150 (West Conshohocken, PA:
ASTM International
, approved April 1,
2020
), https://doi.org/10.1520/C0150-20
39.
Standard Specification for Portland Cement
, AASHTO M85 (Washington, DC:
American Association of State Highway and Transportation Officials
,
2020
).
40.
Standard Test Methods for Determination of the Effects of Biogenic Acidification on Concrete Antimicrobial Additives and/or Concrete Products
, ASTM C1904-20 (West Conshohocken, PA:
ASTM International
, approved October 1,
2020
), https://doi.org/10.1520/C1904-20
41.
Leys
C.
,
Ley
C.
,
Klein
O.
,
Bernard
P.
, and
Licata
L.
, “
Detecting Outliers: Do Not Use Standard Deviation around the Mean, Use Absolute Deviation around the Median
,”
Journal of Experimental Social Psychology
49
, no. 
4
(July
2013
):
764
766
, https://doi.org/10.1016/j.jesp.2013.03.013
42.
Conagin
A.
,
Barbin
D.
, and
Demétrio
C. G. B.
, “
Modifications for the Tukey Test Procedure and Evaluation of the Power and Efficiency of Multiple Comparison Procedures
,”
Scientia Agrícola
65
, no. 
4
(July/August
2008
):
428
432
, https://doi.org/10.1590/S0103-90162008000400016
43.
Driscoll
W. C.
, “
Robustness of the ANOVA and Tukey-Kramer Statistical Tests
,”
Computers & Industrial Engineering
31
, nos.
1–2
(Octoer
1996
):
265
268
, https://doi.org/10.1016/0360-8352(96)00127-1
This content is only available via PDF.
You do not currently have access to this content.