Bainitic bearings, produced through an austempering process, have shown great potential as an alternative to traditional, martensitic bearings. Bainite, specifically lower bainite, which is developed through low-temperature isothermal heat treatment, is a steel microconstituent consisting of carbon supersaturated bainitic ferrite and uniquely oriented, nanosized carbides. In bearing-quality steels, bainite can exceed hardness values of 60 HRC. Due to a uniform transformation, bainitic bearings avoid the formation of tensile residual stresses; the result is significantly reduced distortion and quench cracking compared to martensitic bearings. Because the carbon content of the retained austenite in bainite is higher than the retained austenite in martensite and its morphology is predominately of the film type, the retained austenite is more thermally stable in cold environments, providing designers an opportunity to relax retained austenite volume fraction specifications and to benefit from its mechanical advantages. At the same hardness, bainite tends to have competitive rolling contact fatigue properties and improved fracture toughness when compared to tempered martensite. However, due to the extended transformation time required, austempering heat treatments may be more expensive than traditional martensitic heat treatments. Therefore, researchers have been working on novel austempering variations to shorten the total heat treatment time or significantly increase bearing life. This paper reviews the literature on austempering for bearing applications, compares the microstructure of bainite to tempered martensite and how it impacts bearing performance, and introduces novel austempering variations that have superior rolling contact fatigue lives that may be cost-competitive with traditional martensitic heat treatments.

1.
El Laithy
M.
,
Wang
L.
,
Harvey
T.
,
Vierneusel
B.
,
Correns
M.
, and
Blass
T.
, “
Further Understanding of Rolling Contact Fatigue in Rolling Element Bearings: A Review
,”
Tribology International
140
(
2019
): 105849,
2.
Singh
A.
and
Jadhav
A.
, “
Bearing Market by Type, Size, Distribution Channel, Machine Type, End Use and Group: Global Opportunity Analysis and Industry Forecast, 2020–2027
,” Allied Market Research,
2020
, http://web.archive.org/web/20220727183601/https://www.alliedmarketresearch.com/bearings-market
3.
Hengerer
F.
,
Brockmüller
U.
, and
Sörström
P. O.
, “
Through-Hardening or Case-Hardening for Tapered Roller Bearings?
,” in
Creative Use of Bearing Steels
, ed.
Hoo
J. J.
C.
(
West Conshohocken, PA
:
ASTM International
,
1993
), 21–33,
4.
Bhadeshia
H. K. D.
H.
, “
Steels for Bearings
,”
Progress in Materials Science
57
, no.
2
(February
2012
): 268–435,
5.
Dossett
J. L.
and
Totten
G. E.
, eds.,
ASM Handbook Vol. 4A: Steel Heat Treating Fundamentals and Processes
(
Materials Park, OH
:
ASM International
,
2013
),
6.
Krauss
G.
, “
Tempering of Steel
,” in
Steels: Processing, Structure, and Performance
, 2nd ed. (
Materials Park, OH
:
ASM International
,
2015
), 373–403,
7.
Bhadeshia
H. K. D.
H.
,
Bainite in Steels: Theory and Practice
, 3rd ed. (
London, UK
:
Institute of Materials, Minerals and Mining
,
2015
),
8.
Bhadeshia
H. K. D.
H.
and
Honeycombe
R. W.
K.
, “
The Bainite Reaction
,” in
Steels: Microstructure and Properties
(
Oxford, UK
:
Elsevier, Butterworth-Heinemann
,
2006
), 129–154,
9.
Voothaluru
R.
,
Bedekar
V.
,
Yu
D.
,
Xie
Q.
,
An
K.
,
Pauskar
P.
, and
Hyde
R. S.
, “
Investigating the Difference in Mechanical Stability of Retained Austenite in Bainitic and Martensitic High-Carbon Bearing Steels Using In Situ Neutron Diffraction and Crystal Plasticity Modeling
,”
Metals
9
, no.
5
(
2019
): 482,
10.
Hunkel
M.
,
Dong
J.
,
Epp
J.
,
Kaiser
D.
,
Dietrich
S.
,
Schulze
V.
,
Rajaei
A.
, et al
, “
Comparative Study of the Tempering Behavior of Different Martensitic Steels by Means of In-Situ Diffractometry and Dilatometry
,”
Materials
13
, no.
22
(
2020
): 5058,
12.
Chae
J.
, “
Application of Lower Bainite Microstructure for Bearing Steels and Acceleration of Transformation Kinetics
” (PhD diss.,
Pohang University of Science and Technology
,
2012
).
13.
Blass
T.
,
Dinkel
M.
, and
Trojahn
W.
, “
Bearing Performance as a Function of Structure and Heat Treatment
,”
Materials Science and Technology
32
, no.
11
(January
2016
): 1079–1085,
14.
MacKenzie
D. S.
, “
Development of Residual Stresses during Machining and Workholding
,” Gear Solutions, April
2017
, https://web.archive.org/web/20220805145427/https://gearsolutions.com/departments/hot-seat-development-of-residual-stresses-during-machining-and-workholding/
15.
Reardon
A. C.
,
Freborg
A.
,
Li
Z.
, and
Ferguson
L.
, “
Investigating a Die Quench Cracking Problem in 52100 Steel Bearing Rings with Computer Simulation
,” in
International Manufacturing Science and Engineering Conference
, vol.
1
: Processing (
New York, NY
:
American Society of Mechanical Engineers
,
2016
),
16.
Lee
S. H.
and
Kang
H. J.
, “
Austempering Effects on the Rolling Contact Fatigue Characteristics of Bearing Steels
,” in
Bearing Steel Technologies, 10th Volume: Advances in Steel Technologies for Rolling Bearings
, ed.
Beswick
J.
(
West Conshohocken, PA
:
ASTM International
,
2015
), 1–23,
17.
Luzginova
N.
,
Zhao
L.
, and
Sietsma
J.
, “
Evolution and Thermal Stability of Retained Austenite in SAE 52100 Bainitic Steel
,”
Materials Science and Engineering: A
448
, nos.
1–2
(
2007
): 104–110,
18.
Dong
J.
,
Vetters
H.
,
Hoffman
F.
, and
Zoch
H. W.
, “
Microstructure and Fatigue Strength of the Bearing Steel 52100 after Shortened Bainitic Treatment
,”
Journal of ASTM International
7
, no.
2
(December
2009
): 1–10,
19.
Vetters
H.
,
Dong
J.
, and
Zoch
H. W.
, “
Effect of Residual Austenite on Properties of Tool Steel Following Shortened Treatments in Lower Bainitic Phase
,”
International Heat Treatment and Surface Engineering
3
, no.
4
(
2009
): 130–135,
20.
Sidoroff
C.
,
Perez
M.
,
Dierickx
P.
, and
Girodin
D.
, “
Advantages and Shortcomings of Retained Austenite in Bearing Steels: A Review
,” in
Bearing Steel Technologies, 10th Volume: Advances in Steel Technologies for Rolling Bearings
(
West Conshohocken, PA
:
ASTM International
,
2015
), 312–348,
21.
Chidester
A. J.
,
Darragh
C. V.
,
Hoff
R. C.
,
Imundo
J. R.
,
Maloney
J. L.
 III
, and
Nitescu
D.
, “
Heat Treatment of Bearings
,” in
ASM Handbook Vol. 4D: Heat Treating of Irons and Steels
, ed.
Dossett
J.
and
Totten
G.
(
Materials Park, OH
:
ASM International
,
2014
), 219–240,
22.
Akbasoglu
F. C.
and
Edmonds
D. V.
, “
Rolling Contact Fatigue and Fatigue Crack Propagation in 1C-1.5Cr Bearing Steel in the Bainitic Condition
,”
Metallurgical Transactions A
21
(
1990
): 889–893,
23.
Beswick
J. M.
, “
Fracture and Fatigue Crack Propagation Properties of Hardened 52100 Steel
,”
Metallurgical Transactions A
20
(October
1989
): 1961–1973,
24.
Glover
D.
, “
A Ball-Rod Rolling Contact Fatigue Tester
,” in
Rolling Contact Fatigue Testing of Bearing Steels
, ed.
Hoo
J.
(
West Conshohocken, PA
:
ASTM International
,
1982
), 107–124,
25.
Hampshire
J. M.
,
Nash
J. V.
, and
Hollox
G. E.
, “
Materials Evaluation by Flat Washer Testing
,” in
Rolling Contact Fatigue Testing of Bearing Steels
, ed.
Hoo
J.
(
West Conshohocken, PA
:
ASTM International
,
1982
), 46–66,
26.
Böhmer
H.
, “
Residual Stresses and Material Behavior of M50NiL and RBD
,” in
Creative Use of Bearing Steels
, ed.
Hoo
J. J.
C.
(
West Conshohocken, PA
:
ASTM International
,
1993
), 34–48,
27.
Hollox
G. E.
,
Hobbs
R. A.
, and
Hampshire
J. M.
, “
Lower Bainite Bearings for Adverse Environments
,”
Wear
68
, no.
2
(
1981
): 229–240,
28.
Standard Hardness Conversion Tables for Metals Relationship among Brinell Hardness, Vickers Hardness, Rockwell Hardness, Superficial Hardness, Knoop Hardness, Scleroscope Hardness, and Leeb Hardness
, ASTM E140-12b(
2019
) (
West Conshohocken, PA
:
ASTM International
, approved April 15,
2019
),
29.
Harris
T. A.
and
Kotzalas
M. N.
, “
Failure and Damage Modes in Rolling Bearings
,” in
Advanced Concepts of Bearing Technology
(Boca
Raton, FL
:
Elsevier, CRC Press
,
2006
), 273–302,
30.
Tartaglia
J. M.
,
Lazzari
K. A.
,
Hui
G. P.
, and
Hayrynen
K. L.
, “
A Comparison of Mechanical Properties and Hydrogen Embrittlement Resistance of Austempered vs Quenched and Tempered 4340 Steel
,”
Metallurgical and Materials Transactions A
39
(March
2008
): 559–576,
31.
Baughman
R. A.
, “
Effect of Hardness, Surface Finish, and Grain Size on Rolling-Contact Fatigue Life of M-50 Bearing Steel
,”
Journal of Fluids Engineering
82
, no.
2
(June
1960
): 287–294,
32.
Vetters
H.
,
Dong
J.
,
Bomas
H.
,
Hoffmann
F.
, and
Zoch
H. W.
, “
Microstructure and Fatigue Strength of the Roller-Bearing Steel 100Cr6 (SAE 52100) after Two-Step Bainitisation and Combined Bainitic-Martensitic Heat Treatment
,”
International Journal of Materials Research
97
, no.
10
(
2006
): 1432–1440,
33.
Kilicli
V.
and
Kaplan
M.
, “
Effect of Austempering Temperatures on Microstructure and Mechanical Properties of a Bearing Steel
” (paper presentation, Machines, Technologies, Materials 9th International Congress,
Varnar, Bulgaria
, September
2012
).
34.
Chakraborty
J.
,
Bhattacharjee
D.
, and
Manna
I.
, “
Austempering of Bearing Steel for Improved Mechanical Properties
,”
Scripta Materialia
59
, no.
2
(
2008
): 247–250,
35.
Tomita
Y.
and
Okabayashi
K.
, “
Improvement in Lower Temperature Mechanical Properties of 0.40 Pct C-Ni-Cr-Mo Ultrahigh Strength Steel with the Second Phase Lower Bainite
,”
Metallurgical Transactions A
14
(
1983
): 485–492,
36.
Sourmail
T.
,
Smanio
V.
, and
Auclair
G.
, “
Kinetics of Bainite Formation in 100Cr6 and Similar High-Carbon Steel Grades
,” in
Bearing Steel Technologies, 10th Volume: Advances in Steel Technologies for Rolling Bearings
, ed.
Beswick
J.
(
West Conshohocken, PA
:
ASTM International
,
2015
), 1–11,
37.
Zhang
F.
and
Yang
Z.
, “
Development of and Perspective on High-Performance Nanostructured Bainitic Bearing Steel
,”
Engineering
5
, no.
2
(
2019
): 319–328,
38.
Zhang
P.
,
Zhang
F. C.
,
Yan
Z. G.
,
Wang
T. S.
, and
Qian
L. H.
, “
Rolling Contact Fatigue Property of Low-Temperature Bainite in Surface Layer of a Low Carbon Steel
,”
Materials Science Forum
675–677
(February
2011
): 585–588,
39.
Clark
A.
, “
Comparison of Austempering and Quench-and-Tempering Processes for Carburized Automotive Steels
” (PhD diss.,
University of Windsor
,
2013
).
40.
Lefevre
J.
and
Hayrynen
K.
, “
Austempered Materials for Powertrain Applications
,”
Journal of Materials Engineering and Performance
22
(
2013
): 1914–1922,
41.
Lu
X.
,
Yang
Z.
,
Qian
D.
,
Lan
J.
, and
Hua
L.
, “
Effect of Martensite Pre-Quenching on Bainite Transformation Kinetics, Martensite/Bainite Duplex Microstructures, Mechanical Properties and Retained Austenite Stability of GCr15 Bearing Steel
,”
Journal of Materials Research and Technology
15
(November/December
2021
): 2429–2438,
This content is only available via PDF.
You do not currently have access to this chapter.
Close Modal

or Create an Account

Close Modal
Close Modal