Abstract
Fatigue design recommendations provided by API RP 2SK, ISO 19901-7 and DNVGL-OS-E301 for studless chain links are based on data of steel grades R3 and R4 and mainly of link diameter of 76mm. Mooring systems utilising larger diameter links and higher strength steels (e.g. grade R5) are now in operation. Consequently, industry expressed a need for fatigue test data in seawater of higher steel grade and larger diameter chain to confirm whether the existing fatigue design guidance is applicable. A joint industry project (JIP) was launched by TWI to investigate fatigue performance of high strength and large diameter mooring chain in free corrosion seawater. A test rig was designed and manufactured which was capable of testing studless mooring chain links up to 127mm link diameter under tension-tension loading. Twenty-three full-scale fatigue tests were conducted on high strength steel grades (R4 and R5) and larger diameter chains (76mm and 127mm) generating 72 link failures. Magnetic particle inspections (MPI) were carried out to characterise the location of cracking, crack size and crack growth rate. This paper describes the results obtained in the JIP.