Abstract

Binder Jetting (BJ) has increased in popularity and capability since its development at MIT as it offers advantages such as fast build rates, integrated overhang support, low-power requirements, and versatility in materials. However, defects arise during layer spreading and printing that are difficult to remove during post-processing. Many of these defects are caused by particle rearrangement/ejection during binder deposition. This study explores methods of reducing particle rearrangement and ejection by applying small amounts of moisture to increase the cohesive forces between powder particles. A moisture application system was built using a piezo-electric disk to atomize water to apply a desired liquid to the BJ powder bed without disruption. The moisture is applied after spreading a new layer. Lines of binder were printed using varying droplet spacings and moisture levels. Results show that the moisture delivery system applied moisture levels across the entire application area with a standard deviation under 23%. The moisture levels delivered also had a single position test-to-test uniformity standard deviation under 21%. All tested levels of moisture addition showed mitigation of the balling defects observed in lines printed using dry powder under the same parameters. Moisture addition decreased effective saturation and increased line dimensions (height and width), but lines printed using the smallest amount of moisture tested, showed similar saturation levels and line widths to lines printed in dry powder while still partially mitigating balling.

This content is only available via PDF.
You do not currently have access to this content.