Oil pipelines and gas pipelines operations result in very different pressure fluctuation schemes due to different compressive properties of liquids and gases. Liquid fluids such as oil are less compressible and pressure fluctuations during oil pipelines operations are more frequent and vary over a wide range of magnitudes and frequencies, compared with those during gas pipelines operations. Despite the differences in operating conditions indicated above, both oil pipelines and gas pipelines are susceptible to stress corrosion cracking and corrosion fatigue failures. This investigation was initiated to understand the different crack growth rate behavior of pipeline steels characteristic to the type of pressure fluctuation schemes in near-neutral pH environment, that is, oil pipelines vs. gas pipelines. It was suspected that the similar range of service life between oil pipeline steels and gas pipeline steels could be attributed to a higher rate of direct dissolution at the tip of a crack during gas pipeline operation because of much higher mean pressures, despite their lower crack growth caused by corrosion fatigue. In the case of near-neutral pH stress corrosion cracking, corrosion makes minor contribution to crack growth but produces diffusible hydrogen that interacts with cyclic loading to make cracks grow. This study was performed using specimens with surface cracks, which simulated the following two environmental conditions: 1) fully exposed to the environment, 2) shielded from the environment, exposed to hydrogen only. In Case 1), the specimen surface, on which the surface cracks were made, was fully exposed to a near-neutral pH solution, allowing the occurrence of corrosion at the crack tip. In Case 2), a narrow strip of a coating was applied to prevent the cracks from direct contact with the corrosive solution; however, the cracks were affected by diffusible hydrogen which had been generated as a by-product of corrosion on the adjacent steel surface free of coatings. These specimens were mechanically loaded under different pressure schemes typical of both oil and gas pipeline operations. It has been found that crack growth caused by direct dissolution of crack tip materials is insignificant, regardless of pipeline operating conditions. A much higher crack growth rate, attributed to hydrogen embrittlement, was found under gas transmission conditions, while a higher corrosion fatigue crack growth was found under oil transmission conditions. Based on these findings, strategies on crack growth mitigation, characteristic to each type of pipeline operation are also proposed.
Skip Nav Destination
2018 12th International Pipeline Conference
September 24–28, 2018
Calgary, Alberta, Canada
Conference Sponsors:
- Pipeline Division
ISBN:
978-0-7918-5186-9
PROCEEDINGS PAPER
Differences in Near-Neutral pH Crack Growth Behavior Between Oil Pipelines and Gas Pipelines and Corresponding Crack Growth Mitigation Strategies
Zhezhu Xu,
Zhezhu Xu
University of Alberta, Edmonton, AB, Canada
Search for other works by this author on:
Andrea Daniel,
Andrea Daniel
Enbridge Pipelines, Ltd., Edmonton, AB, Canada
Search for other works by this author on:
Karina Chevil,
Karina Chevil
TransCanada Pipeline, Ltd., Calgary, AB, Canada
Search for other works by this author on:
Erwin Gamboa,
Erwin Gamboa
TransCanada Pipeline, Ltd., Calgary, AB, Canada
Search for other works by this author on:
Weixing Chen
Weixing Chen
University of Alberta, Edmonton, AB, Canada
Search for other works by this author on:
Zhezhu Xu
University of Alberta, Edmonton, AB, Canada
Andrea Daniel
Enbridge Pipelines, Ltd., Edmonton, AB, Canada
Karina Chevil
TransCanada Pipeline, Ltd., Calgary, AB, Canada
Erwin Gamboa
TransCanada Pipeline, Ltd., Calgary, AB, Canada
Weixing Chen
University of Alberta, Edmonton, AB, Canada
Paper No:
IPC2018-78392, V001T03A063; 9 pages
Published Online:
November 6, 2018
Citation
Xu, Z, Daniel, A, Chevil, K, Gamboa, E, & Chen, W. "Differences in Near-Neutral pH Crack Growth Behavior Between Oil Pipelines and Gas Pipelines and Corresponding Crack Growth Mitigation Strategies." Proceedings of the 2018 12th International Pipeline Conference. Volume 1: Pipeline and Facilities Integrity. Calgary, Alberta, Canada. September 24–28, 2018. V001T03A063. ASME. https://doi.org/10.1115/IPC2018-78392
Download citation file:
51
Views
Related Proceedings Papers
Related Articles
Fatigue Crack Growth in 2-1/4-Cr-1Mo Steel Exposed to Hydrogen Containing Gases
J. Eng. Mater. Technol (July,1979)
Experimental Study on Crack Growth Behavior for Austenitic Stainless Steel in High Temperature Pure Water
J. Pressure Vessel Technol (May,1986)
Interaction of Hydrogen Transport and Material Elastoplasticity in Pipeline Steels
J. Pressure Vessel Technol (August,2009)
Related Chapters
A 3D Cohesive Modelling Approach for Hydrogen Embrittlement in Welded Joints of X70 Pipeline Steel
International Hydrogen Conference (IHC 2012): Hydrogen-Materials Interactions
Effect of Thermal Cycling of Zr-1%Nb Fuel Rod Claddings on Hydride Reorientation
Zirconium in the Nuclear Industry: 20th International Symposium