The Mechanical Properties and Friction and Wear Behavior of C/C-SIC Available to Purchase

Carbon fiber reinforced carbon-silicon carbide composites (C/C-SiC) were prepared by chemical volume infiltration (CVI) method and reaction melt infiltration (RMI) technique of silicon liquid to carbon reinforce carbon matrix composites. The friction and wear behaviors of C/C-SiC composites at various loads and sliding speeds were investigated by MRH-3 block-on-ring tribometer at room temperature under water lubricating conditions. Furthermore, the morphologies, phase of the worn surface and the debris were observed, examined and analyzed by scanning electron microscopy (SEM) and energy-dispersive X-ray microanalysis (EDAX) respectively. Experimental results showed that the C/C-SiC composites had a better wear resistence, and the friction coefficient under water lubricated conditions is about 0.02–0.06. The influence of sliding speed on the friction coefficients and the specific wear rate of C/C-SiC is more obvious than that of normal load when the load is less than 200N (inclueded200N). The friction coefficient and the specific wear rate of C/C-SiC decreased as the sliding velocity increased. At the sliding speed higher than 2m/s, the friction coefficient is less than 0.02. The specific wear rates is at a low level about (2×10⁻⁷mm³/Nm–5×10⁻⁸mm³/Nm).