The reforming test using anode materials and the performance analysis of SOFC using pre-reformate gas were performed. When the reformate gas was supplied with steam, the maximum power density showed a relatively small variation compared to performance of SOFC using H2. When pre-reformate gas was supplied into the anode, SOFC which used Rh doped NiO/CGO91 (Ce0.9Gd0.1O2) as an anode material showed more stable performance than SOFC which used NiO/CGO91.