Abstract
This study investigated the durability of four high temperature coatings for use as a Gardon gauge foil coating. Failure modes and effects analysis have identified Gardon gauge foil coating as a critical component for the development of a robust flux gauge for high intensity flux measurements. Degradation of coating optical properties and physical condition alters flux gauge sensitivity, resulting in flux measurement errors. In this paper, four coatings were exposed to solar and thermal cycles to simulate real-world aging. Solar simulator and box furnace facilities at the National Solar Thermal Test Facility (NSTTF) were utilized in separate test campaigns. Coating absorptance and emissivity properties were measured and combined into a figure of merit (FOM) to characterize the optical property stability of each coating, and physical coating degradation was assessed qualitatively using microscope images. Results suggest rapid high temperature cycling did not significantly impact coating optical properties and physical state. In contrast, prolonged exposure of coatings to high temperatures degraded coating optical properties and physical state. Coatings degraded after 1 hour of exposure at temperatures above 400 °C and stabilized after 6–24 hours of exposure. It is concluded that the combination of high temperatures and prolonged exposure provide the energy necessary to sustain coating surface reactions and alter optical and physical coating properties. Results also suggest flux gauge foil coatings could benefit from long duration high temperature curing (> 400 °C) prior to sensor calibration to stabilize coating properties and increase measurement reliability in high flux and high temperature applications.